Menzolit Menzolit® BMC 2300 Unsaturated Polyester UP
| Category | Polymer , Thermoset , Polyester, TS , Thermoset Polyester Glass Filled BMC |
| Manufacturer | Menzolit |
| Trade Name | Menzolit® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Menzolit Menzolit® BMC 2300 Unsaturated Polyester UP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
BMC 2300 is a special BMC with exceptional high fire retardancy. The glass content is set to a level that provides sufficient mouldability with high strength and stiffness properties. Fire retardancy is exceptionally high and the material is not burnable. The high fire retardancy makes it especially suited for switch gear components, for high voltage and high current applications.Information Provided by Menzolit
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 g/cc | 0.0686 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.50 % | <= 0.50 % | ISO 62 |
| Linear Mold Shrinkage | 0.00080 cm/cm | 0.00080 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 31.0 MPa @Temperature 22.0 °C |
4500 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Tensile Strength, Yield | 31.0 MPa @Temperature 22.0 °C |
4500 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Elongation at Yield | 0.00 % | 0.00 % | tensile rupture strain; ISO 527-4 |
| Modulus of Elasticity | 13.0 GPa | 1890 ksi | 25mm flat samples, compression moulded; ISO 527-4 |
| Flexural Strength | 96.0 MPa @Temperature 22.0 °C |
13900 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Flexural Modulus | 10.0 GPa @Temperature 22.0 °C |
1450 ksi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 5.00 GPa | 725 ksi | in plane |
| Charpy Impact, Notched | 2.30 J/cm² | 10.9 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | |
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 155 °C | 311 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 150 °C | >= 302 °F | ISO 75-2 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Glass Transition Temp, Tg | 134 °C | 273 °F | ISO 11357-2 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Oxygen Index | 43 % | 43 % | ISO 4589-2 |
| Glow Wire Test | 960 °C | 1760 °F | IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 4.0 | 4.0 | IEC 60250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Arc Resistance | >= 180 sec | >= 180 sec | ASTM D495 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 150 °C | 275 - 302 °F | Injection moulding, matched metal die |
Users viewing this material also viewed the following:
- Nye Lubricants 728A (RL) Synthetic Oil
- Polimeri Europa Flexirene® FF 25 Butene Copolymer Linear Low Density Polyethylene
- Polymer Resources PC/TP-FR3 Flame Retardant PC/Polyester Alloy
- SABIC Innovative Plastics Lexan® NX07331 PC+ABS (Asia Pacific)
- Vyncolit X655/1 Glass Fiber and Mineral Filled Novolac Phenolic
- Covestro Baydur® 730 IBS Polyurethane Structural Foam RIM, Density 40 pcf, MDI-based 2-Component Liquid System
- Diamond Polymers ABS/PC 8901
- Cheng Yu Plastic FR200GV15 Flame Retardant Nylon 66, 15% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved