Network Polymers Softflex® 8103
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | Network Polymers |
| Trade Name | Softflex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers Softflex® 8103.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.118 g/cc | 1.118 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0062 - 0.01620 cm/cm @Thickness 3.17 mm |
0.0062 - 0.01620 in/in @Thickness 0.125 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0052 - 0.0152 cm/cm @Thickness 3.17 mm |
0.0052 - 0.0152 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 41.5 g/10 min @Load 1.00 kg, Temperature 235 °C |
41.5 g/10 min @Load 2.20 lb, Temperature 455 °F |
Procedure A Condition Q; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 - 80 | 70 - 80 | 10 second dwell; ASTM D2240 |
| 74 - 84 | 74 - 84 | Instantaneous; ASTM D2240 | |
| Elongation at Break | 970 % | 970 % | ASTM D412 |
| Tensile Modulus | 0.02904 GPa | 4.212 ksi | |
| 50% Modulus | 0.0240 GPa | 3.48 ksi | ASTM D412 |
| 100% Modulus | 0.0300 GPa | 4.35 ksi | ASTM D412 |
| 300% Modulus | 0.0430 GPa | 6.24 ksi | ASTM D412 |
| Flexural Modulus | 0.0245 GPa | 3.55 ksi | |
| Gardner Impact | >= 36.2 J @Temperature -30.0 °C |
>= 26.7 ft-lb @Temperature -22.0 °F |
|
| Tear Strength | 63.8 kN/m | 364 pli | |
| Taber Abrasion, mg/1000 Cycles | 0.146 | 0.146 | H22 Wheel 1000 g load/1000 cycles; ASTM D3389 |
| Compression Set | 6.0 % | 6.0 % | Method B, 22 hours at 25% deflection and 23°C; ASTM D395 |
| 74.7 % @Temperature 70.0 °C |
74.7 % @Temperature 158 °F |
22 hours at 25% deflection; ASTM D395, Method B, | |
| 92.2 % @Temperature 100 °C |
92.2 % @Temperature 212 °F |
22 hours at 25% deflection; ASTM D395, Method B, | |
| Tensile Set | 108.3 % | 108.3 % |
Users viewing this material also viewed the following:
- Northstar Polymers MGG-A70DQ High Performance Polyurethane Cast Elastomer System 70A
- Lehigh Technologies 140 Mesh Ground Reclaimed Whole Tire Rubber
- Michelman® Michem® Lube 160 Anionic carnauba wax emulsion
- Universal Wire Works BAg-7 (AMS 4763) Silver Brazing Filler Metal
- Cytec Thornel® T-300 6K Carbon Fiber, Polyacrylonitrile (PAN) Precursor
- China Tungsten YG15X Tungsten Carbide Powder
- Asahi Kasei Thermylene® P6-30FG-0709 30% Fiber Glass Reinforced, Heat Stabilized
- Pyrotek M-8 Fiberseal Blanket
Copyright © lookpolymers.com All Rights Reserved