- MRC Polymers EMAREXâ„¢ 400 GF13 Nylon 6/6, 13% Glass Fiber Filled
MRC Polymers EMAREXâ„¢ 400 GF13 Nylon 6/6, 13% Glass Fiber Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled |
| Manufacturer | MRC Polymers |
| Trade Name | EMAREX™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | MRC Polymers EMAREXâ„¢ 400 GF13 Nylon 6/6, 13% Glass Fiber Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Available in Black onlyCan be UV and Heat StabilizedProperty data for DAM samples.Information provided by MRC Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Filler Content | 11 - 15 % | 11 - 15 % | ASTM D2584 |
| Water Absorption | 1.0 % | 1.0 % | ASTM D570 |
| Relative Viscosity | 50 cP | 50 cP | ASTM D789 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength at Break | 96.5 MPa | 14000 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 159 MPa | 23000 psi | ASTM D790 |
| Flexural Modulus | 4.14 GPa | 600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Temperature 22.8 °C |
0.800 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 265 °C | 509 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 288 - 299 °C | 550 - 570 °F | |
| Middle Barrel Temperature | 277 - 282 °C | 530 - 540 °F | |
| Front Barrel Temperature | 271 - 277 °C | 520 - 530 °F | |
| Nozzle Temperature | 282 - 293 °C | 540 - 560 °F | |
| Melt Temperature | 260 - 282 °C | 500 - 540 °F | |
| Mold Temperature | 65.6 - 121 °C | 150 - 250 °F | |
| Drying Temperature | 85.0 °C | 185 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | |
| Moisture Content | <= 0.18 % | <= 0.18 % | |
| Dew Point | <= -17.8 °C | <= 0.000 °F | |
| Drying Air Flow Rate | 22.7 - 28.3 l/min | 0.800 - 1.00 ft³/min (CFM) | per lb/hour resin processed |
| Injection Pressure | 68.9 - 138 MPa | 10000 - 20000 psi | |
| Back Pressure | 0.000 - 0.517 MPa | 0.000 - 75.0 psi | |
| Cushion | 0.635 cm | 0.250 in | |
| Screw Speed | 30 - 75 rpm | 30 - 75 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Fill Rate | Moderate | |
| Hold Pressure | 40-60% of injection pressure | |
| Packing Pressure | 50-75% of injection pressure |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH GF5020 PD1 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- SABIC Innovative Plastics Lexan® XHT2143 PC Copolymer (Europe-Africa-Middle East)
- Lubriplate Air Tool Lubricant Specialty Oil and Fluid
- SABIC Innovative Plastics Valox® DR51M PBT (Asia Pacific)
- Shin-Etsu Silicones LIMSâ„¢ KEG2002-50A/B Elastomer
- Samsung Cheil Industries Infino® NH-1101 PC/ABS, Unreinforced FR
- Toho Tenax Besfight® MC Type II (12,000 Filament) Nickel Coated Carbon Fiber
- A. Schulman POLYFORT™ FPP 1239H Glass Filled Chemically Coupled Homopolymer Polypropylene
- Eastman Neostar FN006 Elastomer
- Rostone Rosite® 4030FS SMC Thermoset Polyester, 30% Glass Reinforced (discontinued **)
Copyright © lookpolymers.com All Rights Reserved