Techmer ES Plastiblend® PC/PBT IM 5720 A BK
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Techmer ES |
| Trade Name | Plastiblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Plastiblend® PC/PBT IM 5720 A BK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: Impact Modifier and UV StabilizerFeatures: Impact ModifiedAppearance: BlackInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Thickness 3.17 mm |
0.0070 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 113 | 113 | ASTM D785 |
| Tensile Strength, Yield | 48.3 MPa | 7000 psi | ASTM D638 |
| Elongation at Break | 160 % | 160 % | ASTM D638 |
| Flexural Yield Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 5.87 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
11.0 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 7.47 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
14.0 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.4 µm/m-°C | 13.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 245 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering V70W Fluoroelastomer Compound
- Polymer Resources PC-FR2-TFE Polycarbonate, Flame Retardant, 5% PTFE
- Kazanorgsintez PC-075 Polycarbonate
- Silberline Aquavexâ„¢ 1752-207S
- Shinkong Synthetic Fibers Shinite® D202G15 PBT, 15% Glass Filled, Fire Retardant
- Zotefoams Plastazote® LD24FMSV Low Density Polyethylene Foam, Flame Retarded
- ConocoPhillips Syncon® EP Gear Oil, AGMA number 8EP
- Corning 7052 Alkali Barium Borosilicate Crushed/Powdered Glass
- AK Steel 17-4 PH® Precipitation Hardening Stainless Steel, Condition H 925
- Parker Chomerics CHO-SHIELD® 2052 Conductive Coating
Copyright © lookpolymers.com All Rights Reserved