SABIC Innovative Plastics NORYL PX9406P PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PX9406P PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nonbrominated, nonchlorinated, flame retarded. Improved productivity and reliability. 125dc HDT. UL94 V-0 rated. Electrical applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D570 |
| Viscosity | 278000 cP | 278000 cP | Melt Viscosity, 280°C, 1500 sec-1; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 3.9 g/10 min @Load 10.0 kg, Temperature 250 °C |
3.9 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Melt Index of Compound | 10 g/10 min @Load 5.00 kg, Temperature 280 °C |
10 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 23 g/10 min @Load 5.00 kg, Temperature 300 °C |
23 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 | |
| 27 g/10 min @Load 10.0 kg, Temperature 280 °C |
27 g/10 min @Load 22.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | SABIC - Japan Method |
| 73.0 MPa | 10600 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 4.5 % | 4.5 % | 50 mm/min; ISO 527 |
| 85 % | 85 % | SABIC - Japan Method | |
| Flexural Strength | 99.0 MPa | 14400 psi | ASTM D790 |
| Flexural Yield Strength | 108 MPa | 15700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.35 GPa | 341 ksi | ASTM D790 |
| 2.60 GPa | 377 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.66 J/cm | 3.11 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| 8.00 kJ/m² @Temperature -40.0 °C |
3.81 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1A | |
| 9.00 kJ/m² @Temperature -20.0 °C |
4.28 ft-lb/in² @Temperature -4.00 °F |
80*10*4; ISO 180/1A | |
| 10.0 kJ/m² @Temperature -10.0 °C |
4.76 ft-lb/in² @Temperature 14.0 °F |
80*10*4; ISO 180/1A | |
| 11.0 kJ/m² @Temperature 0.000 °C |
5.23 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact Unnotched | 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
38.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| CTE, linear, Parallel to Flow | 66.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 75.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| Hot Ball Pressure Test | <= 125 °C | <= 257 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 136 °C @Thickness 6.40 mm |
277 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 117 °C | 243 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 125 °C @Thickness 6.40 mm |
257 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 142 °C | 288 °F | Rate B/120; ISO 306 |
| 151 °C | 304 °F | Rate A/120; ISO 306 | |
| Flammability, UL94 | V-2 @Thickness 0.400 mm |
V-2 @Thickness 0.0157 in |
UL 94 |
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
UL 94 | |
| 5VA @Thickness 2.50 mm |
5VA @Thickness 0.0984 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 2.8 @Frequency 50.0 - 60.0 Hz |
2.8 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® 4790-92-20 Supported Urethane Foam, Extra Soft, Slow Rebound, PET Reinforced
- Fine Organics FINAWAX VL Lubricant Additive
- Jackon JACKOCELL® R212 Expanded Polystyrene Construction and Block Molding
- Heatbath/Park AL-3 High Speed Hardening Salt
- Haynes 556® alloy, 10% cold reduction, 1121°C anneal for 5 minutes
- Sumitomo Bakelite North America E 8354A-1 Short Glass Fiber Reinforced Epoxy
- A. Schulman POLYBATCH™ White LL8425 AP Concentrate Based In LLDPE
- A. Schulman SCHULAMID® 6 GF15H 15% Glass Fiber Reinforced, Heat Impact Nylon 6
- Alliance Polymers Viprene™ P50A-22U-NAT Thermoplastic Vulcanizate Elastomer
- DuPont Performance Polymers Crastin® CE2055 BK580 PBT (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved