MRC Polymers EMAREXâ„¢ 300 GF33 Nylon 6, 33% Glass Fiber Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | MRC Polymers |
| Trade Name | EMAREX™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | MRC Polymers EMAREXâ„¢ 300 GF33 Nylon 6, 33% Glass Fiber Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Available in Black onlyCan be UV and Heat StabilizedProperty data for DAM samples.Information provided by MRC Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Filler Content | 31 - 35 % | 31 - 35 % | ASTM D2584 |
| Water Absorption | 1.1 % | 1.1 % | ASTM D570 |
| Relative Viscosity | 50 cP | 50 cP | ASTM D789 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength at Break | 157.99 MPa | 22915 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm @Temperature 22.8 °C |
1.10 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 215 °C | 419 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 249 - 271 °C | 480 - 520 °F | |
| Middle Barrel Temperature | 260 - 282 °C | 500 - 540 °F | |
| Front Barrel Temperature | 271 - 293 °C | 520 - 560 °F | |
| Nozzle Temperature | 271 - 293 °C | 520 - 560 °F | |
| Melt Temperature | 260 - 282 °C | 500 - 540 °F | |
| Mold Temperature | 37.8 - 93.3 °C | 100 - 200 °F | Where aesthetics are critical its preferred to use 180-200ºF |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | |
| Moisture Content | <= 0.15 % | <= 0.15 % | |
| Dew Point | <= -17.8 °C | <= 0.000 °F | |
| Drying Air Flow Rate | 22.7 - 28.3 l/min | 0.800 - 1.00 ft³/min (CFM) | per lb/hour resin processed |
| Injection Pressure | 68.9 - 138 MPa | 10000 - 20000 psi | |
| Back Pressure | 0.000 - 0.517 MPa | 0.000 - 75.0 psi | |
| Cushion | 0.635 cm | 0.250 in | |
| Screw Speed | 30 - 75 rpm | 30 - 75 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Fill Rate | Moderate | |
| Hold Pressure | 40-60% of injection pressure | |
| Packing Pressure | 50-75% of injection pressure |
Users viewing this material also viewed the following:
- Oceanchem Group Tris (2-chloroethyl) Phosphate (TCEP)
- SABIC Innovative Plastics LNP LUBRICOMP DFL28 PC (Asia Pacific)
- Ravago Manufacturing Americas Hylac® FR134 ABS
- Solvay TECHNYL® SSD 330 KNF/E PA66, 15% glass filled, DRY
- Techmer ES HiFill® PA6/12 CF30 BK 30% Carbon Filled
- Solvay BRICORR® 288 40% phosphonocarboxylic acid salts
- A. Schulman POLYBATCH™ UVK-90 UV Stabilizer Concentrate Based In Polyethylene
- ExxonMobil 100 Mobil DTE PM Series
- Covestro Makrolon® DP1-1888* Polycarbonate, 20% Glass Filled
- ATI Allegheny Ludlum AL 13-8™ H 1050 Precipitation Hardening Alloy, Heat Treated at 1050°F
Copyright © lookpolymers.com All Rights Reserved