Seals Eastern 5717 Fluorocarbon-Elastomer
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Seals Eastern, Inc |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Seals Eastern 5717 Fluorocarbon-Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FKM. General service.Information provided by Seals Eastern, Inc.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 65 | >= 65 | ASTM D2240, Type A |
| 75 | 75 | AVG; ASTM D2240, Type A | |
| Tensile Strength at Break | >= 9.646 MPa | >= 1399 psi | ASTM D412 Method A |
| 13.4 MPa | 1950 psi | AVG; ASTM D412 Method A | |
| Tensile Strength, Yield | 1.32 MPa | 192 psi | AVG Stress at Elongation M25; ASTM D412 Method A |
| >= 1.58 MPa | >= 229 psi | Stress at Elongation M50; ASTM D412 Method A | |
| 2.15 MPa | 312 psi | AVG Stress at Elongation M50; ASTM D412 Method A | |
| >= 3.41 MPa | >= 494 psi | Stress at Elongation M100; ASTM D412 Method A | |
| 4.47 MPa | 649 psi | AVG Stress at Elongation M100; ASTM D412 Method A | |
| Elongation at Break | >= 158 % | >= 158 % | ASTM D412 Method A |
| 225 % | 225 % | AVG; ASTM D412 Method A | |
| Modulus of Elasticity | 0.01074 GPa | 1.557 ksi | ASTM D412 Method A |
| Shear Modulus | 0.00358 GPa | 0.519 ksi | ASTM D412 Method A |
| Secant Modulus | 0.01009 GPa | 1.463 ksi | ASTM D412 Method A |
| Tear Strength Test | 132 | 132 | (psi); ASTM D624, Die B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Minimum Service Temperature, Air | -18.9 °C | -2.00 °F | Retraction Temperature, TR10; ASTM D1329 |
| Glass Transition Temp, Tg | -20.0 °C | -4.00 °F | ASTM D1329 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Strain Energy / Unit Volume at 20% Elongation (psi) | 20 |
Users viewing this material also viewed the following:
- Palm Labs Adhesives Turbo Fuse Series 150 (500 Viscosity) Rapid Bonding Adhesive
- Qualchem Danamid FES-23 Polyamide 6
- Fiberfil® J-60/40 Polypropylene Homopolymer, 40% Glass Reinforced
- Spartech Korad® SP-2011 Cap/HIPS Polystyrene Sheet
- Solvay ANTAROX® BL 480 Surfactant
- Alcoa MIC-6 Aluminum Mold Alloy
- DSM Arnitel® PM381 Polyether Ester Elastomer (European Grade)
- Akzo Nobel Expancel® 461 DE 40 d60 Dry expanded microspheres
- Assab Steels 8407 2M Hot Work Steel
Copyright © lookpolymers.com All Rights Reserved