MBA Polymers PP 2126 Post-consumer recycled general purpose polypropylene impact copolymer
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer |
| Manufacturer | MBA Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | MBA Polymers PP 2126 Post-consumer recycled general purpose polypropylene impact copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Available in standard black.Information provided by MBA Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | MBA Method |
| Melt Flow | 5.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 20.0 MPa @Temperature 23.0 °C |
2900 psi @Temperature 73.4 °F |
ISO 527-2/50 |
| Flexural Modulus | 1.00 GPa @Temperature 23.0 °C |
145 ksi @Temperature 73.4 °F |
ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -20.0 °C |
2.86 ft-lb/in² @Temperature -4.00 °F |
ISO 180/1A |
| 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 51.0 °C | 124 °F | unannealed; ISO 75-1A |
| Vicat Softening Point | 60.0 °C | 140 °F | VST/B/50; ISO 306 |
| 135 °C | 275 °F | VST/A/50; ISO 306 | |
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
Glow Wire Flammability Index; IEC 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 210 °C | 356 - 410 °F | Extrusion Range |
| 200 °C | 392 °F | Recommended Extrusion | |
| 200 °C | 392 °F | Recommended Injection Molding | |
| 190 - 220 °C | 374 - 428 °F | Injection Molding Range | |
| Mold Temperature | 40.0 °C | 104 °F | Recommended |
| 30.0 - 60.0 °C | 86.0 - 140 °F | ||
| Drying Temperature | 80.0 °C @Time 3600 - 7200 sec |
176 °F @Time 1.00 - 2.00 hour |
|
| Moisture Content | <= 0.10 % | <= 0.10 % |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC (Asia Pacific)
- Chevron Phillips MarFlex® 7120 LLDPE Blown & Cast Film Resin (discontinued **)
- Quadrant EPP Duratron® PEI U2300 Extruded 30% Glass Reinforced Polyetherimide (ASTM Product Data Sheet)
- Karina E 08/26-FC-LMP Beige Color Concentrate for PVC
- Hexcel® HexWeb® CR III 3/16-5056-.002 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Denka REOMER G G5072 Thermoplastic Elastomer, For Extrusion
- Chosun Refractories CTL ASP-S Monolithic Refractories for Ladle and Tundish
- Clariant Renol PBTG30-L Polybutylene Terephthalate, 30% Glass Reinforced
- Unitika elitel UE3600 Polyester, Pellet
- Lubriplate Metal Working Fluid
Copyright © lookpolymers.com All Rights Reserved