SABIC Innovative Plastics LNP THERMOCOMP IF006 PA 6/12
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP IF006 PA 6/12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* IF006 is a compound based on Nylon 6/12 resin containing 30% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| 1.322 g/cc | 0.04776 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.170 % | 0.170 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0011 - 0.0016 cm/cm @Time 86400 sec |
0.0011 - 0.0016 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 - 0.0020 cm/cm @Time 86400 sec |
0.0010 - 0.0020 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0066 - 0.0071 cm/cm @Time 86400 sec |
0.0066 - 0.0071 in/in @Time 24.0 hour |
ISO 294 |
| 0.0070 - 0.0080 cm/cm @Time 86400 sec |
0.0070 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 178 MPa | 25800 psi | ISO 527 |
| 182 MPa | 26400 psi | ASTM D638 | |
| Elongation at Break | 3.4 % | 3.4 % | ISO 527 |
| 3.7 % | 3.7 % | ASTM D638 | |
| Tensile Modulus | 9.58 GPa | 1390 ksi | 50 mm/min; ASTM D638 |
| 10.32 GPa | 1497 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 250 MPa | 36300 psi | ISO 178 |
| 291 MPa | 42200 psi | ASTM D790 | |
| Flexural Modulus | 8.83 GPa | 1280 ksi | ISO 178 |
| 9.30 GPa | 1350 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.38 J/cm | 2.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 12.38 J/cm | 23.19 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 78.0 kJ/m² | 37.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 14.0 J | 10.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
22.5 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 40.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
22.5 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 73.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 73.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C @Thickness 3.20 mm |
388 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- SABIC EPS 650FF Expandable Polystyrene
- Freudenberg Simrit N456 Nitrile Elastomer (NBR)
- Lotte Chemical Titan TITANLENE® LDC801YY Low density polyethylene resin
- SABIC Innovative Plastics LNP THERMOCOMP PF1006HI005 PA 6 (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP THERMOCOMP 9X94104 PEI (Europe-Africa-Middle East)
- Ecomass® 1080TU96 Tungsten Filled Polyamide
- Channel Industries 5500 Lead Zirconate Titanate Piezoelectric
- 3A Composites Core Materials AIREX® R63.50 Damage Tolerant Foam
- 3M 4026 Double Coated Urethane Foam Tape
- A. Schulman POLYFLAM™ FPP 1006S Talc Filled Homopolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved