Qualchem Danamid AFGF-30 Polyamide 66, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Qualchem Zrt. |
| Trade Name | Danamid |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Qualchem Danamid AFGF-30 Polyamide 66, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Reinforced with glass fiberInformation provided by Qualchem Zrt.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | DIN 53479 |
| Filler Content | 28 - 32 % | 28 - 32 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 150 MPa | 21800 psi | 50 mm/min; ISO 527-1,2 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1,2 |
| Tensile Modulus | >= 9.30 GPa | >= 1350 ksi | ISO 527-1,2 |
| Charpy Impact Unnotched | 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
DIN 53453 |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -20.0 °C |
2.86 ft-lb/in² @Temperature -4.00 °F |
DIN 53453 |
| 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 4.00 mm |
HB @Thickness 0.157 in |
MSZ 10383 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Comparative Tracking Index | 375 V | 375 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Content | 1.5 - 1.8 % | 1.5 - 1.8 % | DIN 53714 |
Users viewing this material also viewed the following:
- PolyMirae Moplen EP340G Sheet and Thermoforming Grade Polypropylene
- Chevron Phillips Marlex® CL-200YB (Black) Rotational molding crosslinkable high density polyethylene (discont
- ExxonMobil Escorene® LD-737 EVA Copolymer for Specialty Applications (discontinued **)
- Kraton® NEXAR™ MD9200 Polymer Barrier Membrane
- LATI Later 4 G/30-V0 PBT, 30% Glass Fiber Reinforced, Flame Retardant
- Lehmann & Voss LUVOCOM® 1100/GF/30/NAT Polyether sulfone, with glass fiber
- Techmer ES HiFill® PES GF10 10% Glass Filled
- A. Schulman PP 1248-01 Polypropylene High-Flow Homopolymer Polypropylene
- 3M 25X187 Protective UV Tape
- Solvay Specialty Polymers Algoflon® F5/S PTFE (Polytetrafluoroethylene) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved