SABIC Innovative Plastics LNP Thermotuf VF002 PA 66 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Thermotuf
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermotuf VF002 PA 66 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP THERMOTUF* VF002 is a compound based on Nylon resin containing Glass Fiber. Added features of this material include: High Impact.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.80 %

@Time 86400 sec
0.80 %

@Time 24.0 hour
50% RH; ASTM D 570
Mechanical Properties Metric English Comments
Tensile Strength at Break 64.0 MPa
9280 psi
ASTM D 638
Tensile Strength, Yield 66.0 MPa
9570 psi
ASTM D 638
Elongation at Break 4.1 %
4.1 %
ASTM D 638
Elongation at Yield 65.1 %
65.1 %
ASTM D 638
Flexural Strength 96.0 MPa
13900 psi
ASTM D 790
Flexural Modulus 3.27 GPa
474 ksi
ASTM D 790
Izod Impact, Notched 1.70 J/cm

@Temperature 23.0 °C
3.18 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 8.38 J/cm

@Temperature 23.0 °C
15.7 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
28.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
ASTM E 1530
Deflection Temperature at 1.8 MPa (264 psi) 222 °C

@Thickness 3.20 mm
432 °F

@Thickness 0.126 in
unannealed; ASTM D 648