- Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
- Diamond Polymers ASA T-105
Diamond Polymers ASA T-105
| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ASA T-105.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: ASA Weatherable Polymer, Injection Molding Grade, Medium Heat ResistanceInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 0.30 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.30 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 1.1 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.1 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 88 | 88 | ASTM D785 |
| Tensile Strength, Yield | 37.2 MPa | 5400 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 1.81 GPa | 263 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 1.49 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
2.80 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 87.8 °C | 190 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| 103 °C | 217 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 | |
| Vicat Softening Point | 97.2 °C | 207 °F | 0.125 inch, 1 Kg; ASTM D1525 |
Users viewing this material also viewed the following:
- DuPont™ Clysar® LLP Polyolefin Shrink Packaging Film, 75 Gauge (discontinued **)
- Indium Corp. Indalloy® 254 86.9Sn/10.0In/3.1Ag Lead-Free Solder Alloy
- Techmer ES HiFill® ABS GF20 20% Glass Filled
- Total PSI 3351 High Heat Resistance Impact Polystyrene
- CPT C-Flex® R70-050 Clear Biocompatible TPE
- CTC X-PRO PP 100 P1015 Polypropylene Homopolymer
- Barlog Plastics KEBATER B510 PBT unreinforced
- DuPont Performance Polymers Kalrez® 6230 FFKM Perfluoroelastomer
Copyright © lookpolymers.com All Rights Reserved