Lucite International Diakon® Frost 902 80 Acrylic Polymer
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, General Purpose, Molded |
| Manufacturer | Lucite International |
| Trade Name | Diakon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucite International Diakon® Frost 902 80 Acrylic Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Lucite International
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Melt Flow | 5.8 g/10 min | 5.8 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 89 | 89 | ISO 2039-2 |
| Ball Indentation Hardness | 170 MPa | 24700 psi | ISO 2039-1 (H 961-30) |
| Tensile Strength | 52.0 MPa | 7540 psi | ISO 527 |
| Elongation at Break | 2.6 % | 2.6 % | ISO 527 |
| Flexural Strength | 88.0 MPa | 12800 psi | ISO 178 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 1.40 kJ/m² | 0.666 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.180 J/cm² | 0.857 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | ISO 75B |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75A |
| Vicat Softening Point | 100 °C | 212 °F | ISO 306B |
| 106 °C | 223 °F | ISO 306A | |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 88.8 % | 88.8 % | ASTM D1003 |
| Transmission, Visible | 87.3 % | 87.3 % | ASTM D1003 |
Users viewing this material also viewed the following:
- Rogers Corporation Bisco™ HT-840 Cellular Silicone Foam
- DuPont™ Clysar® EHC Polyolefin Shrink Packaging Film, 50 Gauge (discontinued **)
- Solvay Specialty Polymers Amodel® A-4122 NL WH 905 Polyphthalamide (PPA), 22% Glass Fiber
- Tra-Con Tra-Bond 2126 Black Opaque Epoxy Adhesive
- ConocoPhillips Syncon® 80W-140 HP Synthetic Gear Oil
- CP-Polymer-Technik Wellamid® 6000 GS 15 HWCP 15% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry
- DuPont Performance Polymers Zytel® 79G13HSL NC010 Nylon 66 (Unverified Data**)
- Eliokem Chemigum® P89 Nitrile Elastomer
- Fainplast Compounds PM 55 Flexible PVC, Lead Free
Copyright © lookpolymers.com All Rights Reserved