Lanxess Durethan® TP 036-052 000000 Nylon 6, 60% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 60% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® TP 036-052 000000 Nylon 6, 60% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, injection molding grade, 60% glass fibers, good flowability (Easy Flow), good heat-resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 159 MPa | 23100 psi | Conditioned; ISO 527-1/-2 |
| 240 MPa | 34800 psi | ISO 527-1/-2 | |
| Elongation at Break | 2.6 % | 2.6 % | ISO 527-1/-2 |
| 3.8 % | 3.8 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 12.5 GPa | 1810 ksi | Conditioned; ISO 527-1/-2 |
| 19.3 GPa | 2800 ksi | ISO 527-1/-2 | |
| Impact | 4.3 | 4.3 | Puncture maximum force (N); ISO 6603-2 |
| 3.8 @Temperature -30.0 °C |
3.8 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 1476 J | 1089 ft-lb | ISO 6603-2 |
| 1346 J @Temperature -30.0 °C |
992.8 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 1346 J @Temperature -30.0 °C |
992.8 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 221 °C | 430 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 186 °C | 367 °F | ISO 75-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Oxford Polymers PEI 10GF-Natural PEI, 10% Glass Fiber Reinforced
- PEAK Werkstoff DISPAL S232 Aluminum Alloy, AlSi17Fe4Cu3Mg, Condition T6
- LATI LATAN 23 Polyoxymethylene Copolymer (POM) (discontinued **)
- Kraton® D1102 (SBS) Linear Block Copolymer
- SIDPEC EGYPTENE® HD 6070 UA HDPE Injection Molding
- Samyang Trirex® PC-3025U 12 MFI UV Stabilized Clear Polycarbonate
- SABIC Innovative Plastics LNP STAT-KON KD000 Acetal Copolymer
- Borealis Borcell™ HE4873 High Density Polyethylene
- Plenco 4300 Phenolic, Granular, Injection Molded
- BASF Ultramid® A3EG3 15% Glass Filled PA66 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved