Chase Plastics CP Pryme® NN130M2HS (Dry) Nylon 66, 30% Glass Fiber Reinforced, Lubricated, Heat Stabilized

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer	Chase Plastics
Trade Name	CP Pryme®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chase Plastics CP Pryme® NN130M2HS (Dry) Nylon 66, 30% Glass Fiber Reinforced, Lubricated, Heat Stabilized.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: Good chemical resistanceGood compressive strengthGood creep resistanceFast cycleHeat stabilizedLubricatedHigh rigiditySolvent resistanceHigh strengthForm: PelletsInformation provided by Chase Plastics.

Physical Properties	Metric	English	Comments
Density	1.41 g/cc	0.0509 lb/in³	ASTM D792
Filler Content	30 %	30 %
Water Absorption	0.60 %	0.60 %	At 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0040 cm/cm	0.0040 in/in	0.125 in; ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	ASTM D785
Tensile Strength at Break	148 MPa	21500 psi	ASTM D638
Elongation at Break	3.0 %	3.0 %	ASTM D638
Flexural Strength	207 MPa	30000 psi	ASTM D790
Flexural Modulus	8.96 GPa	1300 ksi	ASTM D790
Izod Impact, Notched	0.854 J/cm	1.60 ft-lb/in	0.125 in; ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	255 °C	491 °F