Lucite International Diakon® CMH454 Acrylic Polymer
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, General Purpose, Molded |
| Manufacturer | Lucite International |
| Trade Name | Diakon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucite International Diakon® CMH454 Acrylic Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Lucite International
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Melt Flow | 0.80 g/10 min | 0.80 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 99 | 99 | ISO 2039-2 |
| Ball Indentation Hardness | 190 MPa | 27600 psi | ISO 2039-1 (H 961-30) |
| Tensile Strength | 85.0 MPa | 12300 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| Flexural Modulus | 3.40 GPa | 493 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 2.20 kJ/m² | 1.05 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 2.60 J/cm² | 12.4 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.220 J/cm² | 1.05 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 71.0 µm/m-°C | 39.4 µin/in-°F | ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | ISO 75B |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | ISO 75A |
| Vicat Softening Point | 108 °C | 226 °F | ISO 306B |
| 115 °C | 239 °F | ISO 306A | |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.49 | 1.49 | ISO 489 |
| Haze | 0.40 % | 0.40 % | ASTM D1003 |
| Transmission, Visible | 92 % | 92 % | ASTM D1003 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 33 PA6, 33% glass fibre
- Radici Radilon® S ERV3808K (cond.) Nylon 6
- Lehmann & Voss LUVOCOM® 80-7655/RD Polyacetal-copolymer, with aramid reinforcement and PTFE, toughness-modified, high viscosity
- Mearthane Durethaneâ„¢ C 95A Polyurethane
- SABIC Innovative Plastics LNP STAT-KON WC003 PBT (Europe-Africa-Middle East)
- Teknor Apex Telcar® TL-1081A Thermoplastic Elastomer
- A. Schulman SCHULAMID® 66 MK4015H 40% Glass Fiber/Mineral Reinforced, Heat Stabilized Nylon 66
- Dow Corning 2-3436 Antifoam Compound
- Colorite Polymers Vinylbond 95-950-60 PVC Compound
Copyright © lookpolymers.com All Rights Reserved