- Victrex® PEEK 650CA30 30% Carbon Fiber Filled, PolyEtherEtherKetone
Victrex® PEEK 650CA30 30% Carbon Fiber Filled, PolyEtherEtherKetone
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled |
| Manufacturer | Victrex |
| Trade Name | PEEK |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Victrex® PEEK 650CA30 30% Carbon Fiber Filled, PolyEtherEtherKetone.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High performance thermoplastic material, 30% carbon fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding and extrusion, low flow, FDA food contact compliant, color black.Typical Application Areas: Applications for higher strength and stiffness in a static or dynamic system. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.Information Provided by VICTREX®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | Crystaline; ISO 1183 |
| Water Absorption at Saturation | 0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
immersion; ISO 62-1 |
| 0.45 % @Temperature 100 °C |
0.45 % @Temperature 212 °F |
immersion; ISO 62-1 | |
| Viscosity | 800000 cP @Temperature 420 °C |
800000 cP @Temperature 788 °F |
melt; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | 415°C nozzle, 200°C tool; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | 415°C nozzle, 200°C tool; ISO 294-4 |
| Spiral Flow | 8.00 cm @Thickness 1.00 mm |
3.15 in @Thickness 0.0394 in |
415°C nozzle, 200°C tool |
| 37.5 cm @Thickness 3.00 mm |
14.8 in @Thickness 0.118 in |
415°C nozzle, 200°C tool |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa @Temperature 275 °C |
7250 psi @Temperature 527 °F |
ISO 527 |
| 85.0 MPa @Temperature 175 °C |
12300 psi @Temperature 347 °F |
ISO 527 | |
| 150 MPa @Temperature 125 °C |
21800 psi @Temperature 257 °F |
ISO 527 | |
| 250 MPa @Temperature 23.0 °C |
36300 psi @Temperature 73.4 °F |
ISO 527 | |
| Elongation at Break | 1.9 % | 1.9 % | ISO 527 |
| Tensile Modulus | 25.0 GPa | 3630 ksi | ISO 527 |
| Flexural Strength | 60.0 MPa @Temperature 275 °C |
8700 psi @Temperature 527 °F |
ISO 178 |
| 120 MPa @Temperature 175 °C |
17400 psi @Temperature 347 °F |
ISO 178 | |
| 250 MPa @Temperature 125 °C |
36300 psi @Temperature 257 °F |
ISO 178 | |
| 370 MPa @Temperature 23.0 °C |
53700 psi @Temperature 73.4 °F |
ISO 178 | |
| Flexural Modulus | 21.5 GPa | 3120 ksi | ISO 178 |
| Compressive Strength | 60.0 MPa @Temperature 200 °C |
8700 psi @Temperature 392 °F |
ISO 604 |
| 180 MPa @Temperature 120 °C |
26100 psi @Temperature 248 °F |
ISO 604 | |
| 280 MPa @Temperature 23.0 °C |
40600 psi @Temperature 73.4 °F |
ISO 604 | |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180/A |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | ISO 180/U |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | ISO 179/1U |
| Charpy Impact, Notched | 1.05 J/cm² | 5.00 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 µm/m-°C @Temperature <=143 °C |
27.8 µin/in-°F @Temperature <=289 °F |
Average below Tg; ASTM D696 |
| 135 µm/m-°C @Temperature >=143 °C |
75.0 µin/in-°F @Temperature >=289 °F |
Average above Tg; ASTM D696 | |
| CTE, linear, Parallel to Flow | 6.00 µm/m-°C @Temperature <=143 °C |
3.33 µin/in-°F @Temperature <=289 °F |
Below Tg; ASTM D696 |
| 6.00 µm/m-°C @Temperature >=143 °C |
3.33 µin/in-°F @Temperature >=289 °F |
Above Tg; ASTM D696 | |
| Thermal Conductivity | 0.950 W/m-K | 6.59 BTU-in/hr-ft²-°F | Average; ISO 22007-4 |
| 2.00 W/m-K | 13.9 BTU-in/hr-ft²-°F | Along flow; ISO 22007-4 | |
| Melting Point | 343 °C | 649 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 333 °C | 631 °F | ISO 75A-f |
| Glass Transition Temp, Tg | >= 143 °C | >= 289 °F | Onset; ISO 11357 |
| 150 °C | 302 °F | Midpoint; ISO 11357 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1e+05 | 1e+05 | 1V; IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 100 °C | <= 212 °F | Hopper Temperature |
| Nozzle Temperature | 415 °C | 779 °F | |
| Mold Temperature | 180 - 210 °C | 356 - 410 °F | |
| Dry Time | 3.00 hour @Temperature 150 °C |
3.00 hour @Temperature 302 °F |
|
| 5.00 hour @Temperature 120 °C |
5.00 hour @Temperature 248 °F |
Users viewing this material also viewed the following:
- Nyco M400 WOLLASTOCOAT® Wollastonite
- KB Alloys Ticar® 3% Ti - 0.3% C Titanium Carbon Aluminum Rod
- LG Chemical MB838A Opaque impact modifier
- Mitsubishi Xantar® F 22 R Polycarbonate
- LyondellBasell Higlass PF072-3 Polypropylene Homopolymer, 30% Glass Fiber
- Techmer ES Plaslube® J-4/30/TF/15 Nylon 612, 30% GFR, 15% PTFE
- Teknor Apex APEX® 3611-95 Polyvinyl Chloride, Flexible
- DuPont Teijin Films Mylar® RSX Polyester Film, 140 Gauge
- 3M Scotchkote™ 80EG 531 Urethane Elastomer
Copyright © lookpolymers.com All Rights Reserved