- Lubrizol Estane® 2103-90AE Thermoplastic Polyurethane Elastomer
Lubrizol Estane® 2103-90AE Thermoplastic Polyurethane Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | ESTANE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Estane® 2103-90AE Thermoplastic Polyurethane Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Formerly PellethaneAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 7.0 g/10 min @Load 8.70 kg, Temperature 224 °C |
7.0 g/10 min @Load 19.2 lb, Temperature 435 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 90 | 90 | ASTM D2240 |
| Hardness, Shore D | 47 | 47 | ASTM D2240 |
| Tensile Strength, Ultimate | 38.2 MPa | 5540 psi | ASTM D1238 |
| Elongation at Break | 530 % | 530 % | ASTM D412 |
| 50% Modulus | 0.00630 GPa | 0.914 ksi | ASTM D412 |
| 100% Modulus | 0.00970 GPa | 1.41 ksi | ASTM D412 |
| 300% Modulus | 0.0179 GPa | 2.60 ksi | ASTM D412 |
| Flexural Modulus | 0.0695 GPa | 10.1 ksi | ASTM D790 |
| Tear Strength | 133 kN/m | 759 pli | Die C; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 50 | 50 | H22 Wheel, 1000g; ASTM D1044 |
| Compression Set | 25 % @Temperature 25.0 °C, Time 79200 sec |
25 % @Temperature 77.0 °F, Time 22.0 hour |
ASTM D395, Method B |
| 40 % @Temperature 70.0 °C, Time 79200 sec |
40 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395, Method B | |
| Tensile Set | 60 % | 60 % | Elongation set after break; ASTM D412 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 155 µm/m-°C @Temperature 20.0 °C |
86.1 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Vicat Softening Point | 90.6 °C | 195 °F | 120°C/hr, 9.8N; ASTM D1525 |
| Glass Transition Temp, Tg | -34.0 °C | -29.2 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 210 °C | 379 - 410 °F | Molding |
| Mold Temperature | 86.7 - 95.6 °C | 188 - 204 °F | |
| Drying Temperature | 88.0 - 104 °C | 190 - 219 °F | air dew point <-40°C |
Users viewing this material also viewed the following:
- Nye Lubricants 186B (SO) Synthetic Oil
- Polimeri Europa KOBLEND HI PD 19 PBT+PC, Impact Grade (discontinued **)
- ITW Plexus Plexusâ„¢ MA1025 Methacrylate Adhesive
- Dow Corning SILASTIC® 24020-V NATURAL SILICONE RUBBER
- Dow Corning SYL-OFF® 2-7131 FAST CURE ADDITIVE
- CP-Polymer-Technik Wellamid® 6000 MRGV 25/15 HWCP 25% Mineral and 15% Glass Fiber Nylon 6, Heat Stabilized, Dry
- E-Polymers EFLEX® M400 PP Homopolymer
- Arkema Group Orgalloy® LT 6040ISH Nylon (Conditioned)
- BASF Capron® 8203C HS Blend Nylon 6 (Dry) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved