Samyang Trilen® 9550T30 Polypropylene, Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Samyang |
| Trade Name | Trilen® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Trilen® 9550T30 Polypropylene, Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mechanical strength and thermal resistance are excellent.9550T30 is a non-flame retardant, reinforced grade.Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Melt Flow | 23 g/10 min | 23 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 28.9 MPa | 4200 psi | ASTM D638 |
| Elongation at Break | 22 % | 22 % | ASTM D638 |
| Flexural Yield Strength | 40.7 MPa | 5900 psi | ASTM D790 |
| Flexural Modulus | 3.04 GPa | 441 ksi | ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm @Thickness 3.17 mm |
0.918 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 134 °C | 273 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Hyosung Topilene C600M PP
- Mallard Creek Polymers Tylac® 4901 Self Stabilizing Latex
- Schott N-SF57 Glass
- Teknor Apex TruVis Esters™ DIOA Di-IsoOctyl Adipate
- Universal Wire Works A286 (AMS 5804) Filler Metal
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 60 PHR N330 Filler
- Diamond Polymers NPP30-0500 GF20 20% Glass Filled Black Homopolymer Polypropylene
- Arlon 514B12R006 0.006" Cured Silicone Rubber with Fiberglass Substrate
- Aclo Accutech Polypropylene Copolymer HP0334W30L Wollastonite Reinforced
- PolyOne Synprene® RT-3830M Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved