Lehmann & Voss LUVOCOM® PA66/TF/40 Polyamide 66, with PTFE
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® PA66/TF/40 Polyamide 66, with PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteristics.Bearings, sleeves, sliding elements, control disks, gear wheels, duty parts in switches.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.015 - 0.025 cm/cm | 0.015 - 0.025 in/in | |
| Melt Flow | <= 14.3 g/10 min @Load 2.16 kg, Temperature 300 °C |
<= 14.3 g/10 min @Load 4.76 lb, Temperature 572 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 89.0 MPa | 12900 psi | |
| Elongation at Yield | 5.5 % | 5.5 % | |
| 7.0 % | 7.0 % | flexural | |
| Modulus of Elasticity | 2.40 GPa | 348 ksi | |
| Flexural Strength | 125 MPa | 18100 psi | |
| Flexural Modulus | 2.00 GPa | 290 ksi | |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | flatwise; ISO 179 1fU |
| 6.30 J/cm² @Temperature -30.0 °C |
30.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179 1eA |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 179 eA | |
| Coefficient of Friction, Dynamic | 0.070 | 0.070 | |
| Coefficient of Friction, Static | 0.060 | 0.060 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
| 130 °C | 266 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | |
| Vicat Softening Point | 200 °C | 392 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+10 ohm | >= 1.00e+10 ohm | |
| Insulation Resistance | >= 1.00e+11 ohm | >= 1.00e+11 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 290 °C | 554 °F | mass temp |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | |
| Zone 1 | 290 - 310 °C | 554 - 590 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 57600 sec |
167 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (white) |
Users viewing this material also viewed the following:
- Precision Polymer Engineering E70B Ethylene Propylene Rubber
- Ovation Polymers SOFTAPLAS™ S 65A Thermoplastic Elastomer
- Iran Petrochemical (PCC) 16503 Linear Low Density Polyethylene
- Solvay Technyl Starâ„¢ S 218 V30 30% Glass Reinforced Nylon 6
- DuPont Conpol™ 13B Ethylene-Methacrylic Acid Additive Resin
- EMS-Griltech Grilon® BA 140 White Nylon 66/CoPA Bi-Component Fiber
- Asia Technology Pioneers CAP 102 PP Nanocomposite
- SABIC Innovative Plastics Noryl FN215D PPE+HIPS (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved