Sax Polymers SAXAMID 126F9 Nylon 6, 45% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 126F9 Nylon 6, 45% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 126F9 is a polyamide 6 injection-molding-grade reinforced with 45% glass fibers.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 202 MPa | 29300 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 13.7 GPa | 1990 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 317 MPa | 46000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 10.7 GPa | 1550 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 14.0 kJ/m² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 81.0 kJ/m² @Temperature -30.0 °C |
38.5 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 84.0 kJ/m² @Temperature 23.0 °C |
40.0 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 8.70 J/cm² @Temperature -30.0 °C |
41.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 8.80 J/cm² @Temperature 23.0 °C |
41.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C | 412 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 216 °C | 421 °F | B/120; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 121 PC (Asia Pacific)
- Noltex Soarnol® H4815 Ethylene Vinyl Alcohol Copolymer
- LG Chemical SBR 1739 High Acrylonitrile Polymer
- Special Metals NIMONIC® Alloy 81
- SABIC Innovative Plastics LNP STAT-KON RE004 PA 66 (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ Green 3251V Concentrate Based In Polyethylene
- EOS MS1 Maraging Steel for DMLS 3D Printing
- ExxonMobil HD 6706.62 Injection Molding Resin
- Chase Plastics CP Pryme® N233GL (COND, 50% RH) Nylon 6, 33% Glass Fiber Reinforced, Internally Lubricated
- Materion Beryllium Copper Alloy 3 Strip; AT (TF00) Temper (UNS C17510)
Copyright © lookpolymers.com All Rights Reserved