Lehmann & Voss LUVOCOM® 80-7884 Polyacetal-copolymer, with carbon fiber
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 80-7884 Polyacetal-copolymer, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; low thermal coefficient of expansion.Electrically conductive, suitable for continuous discharging of statically generated electricity.High dimensionally stable precision parts.Transporting equipment for electrically sensible goods.No change of electric potential at bearings in case of separation of charge caused by transport and guiding of paper and foil.No mass temperature above 215°C! Ventilation of machinery is recommended.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.47 g/cc | 1.47 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | |
| Melt Flow | 7.35 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.35 g/10 min @Load 4.76 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 90.0 MPa | 13100 psi | |
| Elongation at Yield | 1.0 % | 1.0 % | |
| 1.2 % | 1.2 % | flexural | |
| Modulus of Elasticity | 14.0 GPa | 2030 ksi | |
| Flexural Strength | 125 MPa | 18100 psi | |
| Flexural Modulus | 12.0 GPa | 1740 ksi | |
| Charpy Impact Unnotched | 1.80 J/cm² | 8.57 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| 120 °C | 248 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 173 °C | 343 °F | |
| Flammability, UL94 | HB | HB | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1000 ohm | <= 1000 ohm | |
| Insulation Resistance | <= 100 ohm | <= 100 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | mass temp |
| Nozzle Temperature | 175 - 200 °C | 347 - 392 °F | |
| Zone 1 | 175 - 190 °C | 347 - 374 °F | |
| Zone 2 | 185 - 205 °C | 365 - 401 °F | |
| Zone 3 | 180 - 200 °C | 356 - 392 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 7200 - 28800 sec |
167 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| 120 °C @Time 7200 - 14400 sec |
248 °F @Time 2.00 - 4.00 hour |
Air-Circulation Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Polyplastic Armlen® PP MF 25-3-901 Polypropylene, 20% Mineral Filled
- Phillips 66 COPYLENE® CH042L Polypropylene, Homopolymer, Straw and Extrusion, Antistat
- Gharda Chemicals Gafone S S1430SP60 Polysulfone (PS) (discontinued **)
- Haynes HR-160® alloy plate, aged 8000 hours at 649°C (1200°F)
- Saint-Gobain CHR® SG33-06(R) Industrial Glass-PTFE Backing Acrylic Adhesive Pressure Sensitive Tape
- Techmer ES Plastiblend® PA6 GF20 RM-B L NAT Nylon 6
- ChevronTexaco Elite-Cut® NM Metal Working Fluid
- Covestro Texin® 260 Urethane Thermoplastic Elastomer
- BASF Elastollan® C-95A Polyester Type Polyurethane Elastomer
- Arlon 44602M020 0.020" (0.508 mm) Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved