Chosun Refractories INCT-120S Light-Weight Castable
| Category | Ceramic |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories INCT-120S Light-Weight Castable.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 2.41e-7 - 0.000491 GPa @Temperature 110 °C, Time 86400 sec |
0.0000349 - 0.0711 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.0004905 - 0.0024525 GPa @Temperature 500 °C, Time 10800 sec |
0.07114 - 0.35571 ksi @Temperature 932 °F, Time 3.00 hour |
||
| 0.0014715 - 0.0034335 GPa @Temperature 1000 °C, Time 10800 sec |
0.21343 - 0.49799 ksi @Temperature 1830 °F, Time 3.00 hour |
||
| Compressive Strength | 2.94 - 7.85 MPa @Temperature 110 °C, Time 86400 sec |
427 - 1140 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 2.94 - 7.85 MPa @Temperature 500 °C, Time 10800 sec |
427 - 1140 psi @Temperature 932 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 2.94 - 7.85 MPa @Temperature 1000 °C, Time 10800 sec |
427 - 1140 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.233 W/m-K @Temperature 260 °C |
1.61 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
| 0.2792 W/m-K @Temperature 540 °C |
1.934 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| 0.3257 W/m-K @Temperature 800 °C |
2.257 BTU-in/hr-ft²-°F @Temperature 1470 °F |
||
| Maximum Service Temperature, Air | 1200 °C | 2190 °F | limited |
| Shrinkage | -0.350 % @Temperature 1000 °C, Time 10800 sec |
-0.350 % @Temperature 1830 °F, Time 3.00 hour |
|
| -0.0600 % @Temperature 110 °C, Time 86400 sec |
-0.0600 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 33 % | 33 % | |
| SiO2 | 43 % | 43 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting, Troweling | |
| Main Applications | High temperature Low thermal conductivity | |
| Material Required for Estimating (kg/?) | 900 | |
| Water Required for Casting(%) | 40-50 |
Users viewing this material also viewed the following:
- Network Polymers NPS 90-0645 Super High Impact Polystyrene
- ITW Devcon Metal Repair Titanium Putty, Grey
- Lanxess Durethan® B 40 F 000000 Nylon 6, Film Grade
- Shin-Etsu Silicones KE-3472T Silicone, RTV Conformal Coating
- Samsung Cheil Industries Infino® AR-9301 PA, Glass Filled General Purpose
- Williams Advanced Alloys C110 Solder
- Azoty Tarnow™ TARNOFORM 500 UV POM
- 3M Scotchkote™ FG 512 Epoxy Ceramic Surfacer
Copyright © lookpolymers.com All Rights Reserved