- Lehmann & Voss LUVOCOM® 1/AR/5/NT Polyamide 66, with aramid reinforcement
Lehmann & Voss LUVOCOM® 1/AR/5/NT Polyamide 66, with aramid reinforcement
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Aramid Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1/AR/5/NT Polyamide 66, with aramid reinforcement.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved wear behaviour, low warpage.Isotropic shrinkage characteristics.Control disks, cams, sliding elements and other duty parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0070 - 0.013 cm/cm | 0.0070 - 0.013 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 85.0 MPa | 12300 psi | |
| Elongation at Yield | 5.5 % | 5.5 % | |
| 6.5 % | 6.5 % | flexural | |
| Modulus of Elasticity | 3.50 GPa | 508 ksi | |
| Flexural Strength | 130 MPa | 18900 psi | |
| Flexural Modulus | 3.00 GPa | 435 ksi | |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | flatwise; ISO 179 1fU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
| 130 °C | 266 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 290 °C | 554 °F | mass temp |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | |
| Zone 1 | 290 - 310 °C | 554 - 590 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 57600 sec |
167 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (yellow) |
Users viewing this material also viewed the following:
- MV Labs TB200 TbBr3·xH2O Terbium bromide hydrate
- Polymer Resources PPX/NY G10 PPO/Nylon 66 Alloy , 10% Glass Reinforced
- Kingfa JH710 G20 Flame Retardant & 20% Glass Fiber Reinforced PC
- Sumitomo Bakelite Sumikon® PM-9501 Glass-Filled Phenolic, Compression Grade
- BASF Ultramid® HFX 37 PA6 (Dry)
- Advanced Polymer Alloys DuraGrip™ 6150 BK Melt Processable Elastomer
- 3M FM022R Indoor UL Recognized Clear Polyester Overlaminate Label Product
- BASF Polystyrol® 454 C Impact Grade Polystyrene (Europe)
- ATI Allegheny Ludlum Stainless Steel Free Machining Grade Type 416, Tempered at 760°C (UNS S41600)
- Schmolz + Bickenbach MoldMAX XL® Copper Alloy
Copyright © lookpolymers.com All Rights Reserved