Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 16% Plasticizer (discontinued **)

Category	Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate Butyrate, Molded
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 16% Plasticizer (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and ToysProcessing: Injection Molding (Melt Temperature: 415°F, Mold Temperature: 110°F)Data supplied by Albis Plastics Corporation.

Physical Properties	Metric	English	Comments
Density	1.17 g/cc	0.0423 lb/in³	ASTM D792
Water Absorption	1.2 %	1.2 %	(24 hr); ASTM D570
Linear Mold Shrinkage	0.0015 - 0.0070 cm/cm	0.0015 - 0.0070 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	24.1 MPa	3500 psi	ASTM D638
Tensile Strength, Yield	17.2 MPa	2490 psi	ASTM D638
Flexural Yield Strength	24.1 MPa	3500 psi	ASTM D790
Flexural Modulus	0.930 GPa	135 ksi	ASTM D790
Izod Impact, Notched	3.63 J/cm	6.80 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	54.0 °C	129 °F	ASTM D648
Vicat Softening Point	82.0 °C	180 °F	ASTM D1525

Processing Properties	Metric	English	Comments
Melt Temperature	213 °C	415 °F	Injection
Mold Temperature	43.0 °C	109 °F