Lehmann & Voss LUVOCOM® 19-7342 Polyamide 46, with carbon fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 46 |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 19-7342 Polyamide 46, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia compared with metal parts.Low warpage.Electrically conductive, suitable for continuous discharging of statically generated electricity.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 225 MPa | 32600 psi | |
| Elongation at Yield | 1.8 % | 1.8 % | |
| 2.2 % | 2.2 % | flexural | |
| Modulus of Elasticity | 20.0 GPa | 2900 ksi | |
| Flexural Strength | 320 MPa | 46400 psi | |
| Flexural Modulus | 18.0 GPa | 2610 ksi | |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 150 °C | 302 °F | |
| 160 °C | 320 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1000 ohm | <= 1000 ohm | |
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 310 °C | 590 °F | mass temp |
| Nozzle Temperature | 280 - 330 °C | 536 - 626 °F | |
| Zone 1 | 285 - 315 °C | 545 - 599 °F | |
| Zone 2 | 305 - 315 °C | 581 - 599 °F | |
| Zone 3 | 305 - 315 °C | 581 - 599 °F | |
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 43200 sec |
176 °F @Time 2.00 - 12.0 hour |
Vacuum Dryer |
| 80.0 °C @Time 7200 - 28800 sec |
176 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- PolyOne Stat-Tech™ NN-40CF/000 FRV0 Natural Polyamide 66 (Nylon 66)
- 3M Dyneon™ Fluorel™ FC-2261Q Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- Overview of materials for Nylon 66, Glass/Carbon Fiber Filled
- Greene Tweed Arlon® 1263 PEEK, Carbon Filled
- SABIC Innovative Plastics LNP THERMOCOMP OF008A PPS - Branched
- CLAL-MSX ARCAP Anticorrosion AP4 H11 1/4 hard, Drawn Copper Alloy
- Arkema Group Rilsan® BMN Y TLD Nylon 11, MoS2 Filled (Dry)
- A.D. Compound Adene NCWA Homopolymer 60% CaCO3 Filled Polypropylene
- BASF Sicotan® Yellow K 1010 Color Additive
Copyright © lookpolymers.com All Rights Reserved