SABIC Innovative Plastics Xenoy® XL1339 PC+PET (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xenoy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Xenoy® XL1339 PC+PET (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
XENOY XL1339 is an unreinforced amorphous PC+PET blend, offering excellent impact performance over a wide temperature range. It combines very good flow characteristics with high heat resistance. XENOY XL1339 has excellent dimension stability, good adhesion to PU based glues and paints, and good UV resistance. XENOY XL1339 was developed for automotive applications like A-pillars, painted and unpainted doorhandles, front grills, etc.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.22 g/cc
0.0441 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.70 %

@Temperature 23.0 °C
 0.70 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm
0.0050 - 0.0080 in/in
on tensile bar; SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0080 cm/cm
0.0050 - 0.0080 in/in
on tensile bar; SABIC Method
Melt Flow 4.0 g/10 min

@Load 1.20 kg,
Temperature 265 °C
 4.0 g/10 min

@Load 2.65 lb,
Temperature 509 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 95.0 MPa
13800 psi
ISO 2039-1
Tensile Strength at Break 40.0 MPa
5800 psi
50 mm/min; ISO 527
Tensile Strength, Yield 55.0 MPa
7980 psi
50 mm/min; ISO 527
Elongation at Break 70 %
70 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
50 mm/min; ISO 527
Tensile Modulus 2.30 GPa
334 ksi
1 mm/min; ISO 527
Flexural Yield Strength 80.0 MPa
11600 psi
2 mm/min; ISO 178
Flexural Modulus 2.20 GPa
319 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 15.0 kJ/m²

@Temperature -40.0 °C
 7.14 ft-lb/in²

@Temperature -40.0 °F
 80*10*4; ISO 180/1A
25.0 kJ/m²

@Temperature -30.0 °C
 11.9 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
35.0 kJ/m²

@Temperature -20.0 °C
 16.7 ft-lb/in²

@Temperature -4.00 °F
 80*10*4; ISO 180/1A
38.0 kJ/m²

@Temperature -10.0 °C
 18.1 ft-lb/in²

@Temperature 14.0 °F
 80*10*4; ISO 180/1A
40.0 kJ/m²

@Temperature 23.0 °C
 19.0 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
1.00 J/cm²

@Temperature -20.0 °C
 4.76 ft-lb/in²

@Temperature -4.00 °F
 ISO 179/2C
3.50 J/cm²

@Temperature -30.0 °C
 16.7 ft-lb/in²

@Temperature -22.0 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
4.50 J/cm²

@Temperature 23.0 °C
 21.4 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
5.00 J/cm²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/2C
Taber Abrasion, mg/1000 Cycles 20

@Load 1.00 kg
 20

@Load 2.20 lb
 CS-17; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 75.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 41.7 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 44.4 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
Thermal Conductivity 0.180 W/m-K
1.25 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 125 °C
257 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 105 °C
221 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 130 °C
266 °F
Rate B/50; ISO 306
135 °C
275 °F
Rate B/120; ISO 306
140 °C
284 °F
Rate A/50; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 UL 94 by SABIC-IP
Glow Wire Test 750 °C

@Thickness 2.70 mm
 1380 °F

@Thickness 0.106 in
 Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 3.1

@Frequency 1.00e+6 Hz
 3.1

@Frequency 1.00e+6 Hz
 IEC 60250
3.3

@Frequency 50.0 - 60.0 Hz
 3.3

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 17.0 kV/mm

@Thickness 3.20 mm
 432 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
Dissipation Factor 0.0020

@Frequency 50.0 - 60.0 Hz
 0.0020

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.020

@Frequency 1.00e+6 Hz
 0.020

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2