Unitika A175G15 PA66, 15% Glass Fiber Reinforced, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A175G15 PA66, 15% Glass Fiber Reinforced, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 3.20 mm |
0.0060 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm @Thickness 3.20 mm |
0.015 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-1/-2 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-1/-2 |
| Tensile Modulus | 5.70 GPa | 827 ksi | ISO 527-1/-2 |
| Flexural Strength | 188 MPa | 27300 psi | ISO 178 |
| Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 42.0 µm/m-°C | 23.3 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C | 486 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 229 °C | 444 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.840 mm |
HB @Thickness 0.0331 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 33.0 kV/mm @Thickness 1.00 mm |
838 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
Users viewing this material also viewed the following:
- MV Labs SM700 Sm(NO3)3·6H2O Samarium nitrate hexahydrate
- LG Chemical LUPOL TE-5108 Thermoplastic Elastomer Alloy, 10% Polymer Alloy, High Flow
- IRPC Polimaxx Pentfoam 193L Expandable Polystyrene
- Lehmann & Voss LUVOCOM® 1100/GF/20/EM/MR Polyether sulfone, with glass fiber, easy flowing, demolding aid
- Teijin Panlite® LV-2250Z Transparent and Weather Resistant grade Polycarbonate Resin
- Total HDPE BM961 High Density Polyethylene, High Gloss Blow Molding Resin
- ELASTO UK Dryflex® 602300S SEBS Based Material, Filled Qualities, 30A Hardness, Black
- ExxonMobil Bicor™ 20MB666 OPP Film
- BASF Lupranate® 81 Isocyanate
Copyright © lookpolymers.com All Rights Reserved