Lehmann & Voss LUVOCOM® 1-7003 Polyamide 66, with carbon fiber and PTFE, heat stabilized

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Carbon Fiber/PTFE Filled
Manufacturer	Lehmann & Voss & Co.
Trade Name	LUVOCOM®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lehmann & Voss LUVOCOM® 1-7003 Polyamide 66, with carbon fiber and PTFE, heat stabilized.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Electrically conductive, suitable for continuous discharging of statically generated electricity.Improved friction and wear behaviour. Emergency running property.High dimensionally stable precision parts with low warpage and narrow tolerance range.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG

Physical Properties	Metric	English	Comments
Specific Gravity	1.23 g/cc	1.23 g/cc	ISO 1183
Water Absorption	<= 1.0 %	<= 1.0 %	23°C/24h
Linear Mold Shrinkage	0.0010 - 0.0040 cm/cm	0.0010 - 0.0040 in/in

Mechanical Properties	Metric	English	Comments
Tensile Stress	205 MPa	29700 psi
Elongation at Yield	2.4 %	2.4 %
	3.6 %	3.6 %	flexural
Modulus of Elasticity	12.5 GPa	1810 ksi
Flexural Strength	305 MPa	44200 psi
Flexural Modulus	11.0 GPa	1600 ksi
Charpy Impact Unnotched	4.50 J/cm²	21.4 ft-lb/in²	flatwise; ISO 179 1fU
	4.00 J/cm² @Temperature -30.0 °C	19.0 ft-lb/in² @Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	1.20 J/cm²	5.71 ft-lb/in²	ISO 179 1eA
	0.900 J/cm² @Temperature -30.0 °C	4.28 ft-lb/in² @Temperature -22.0 °F	ISO 179 eA
Coefficient of Friction, Dynamic	0.19	0.19
Coefficient of Friction, Static	0.16	0.16

Thermal Properties	Metric	English	Comments
CTE, linear	25.0 µm/m-°C	13.9 µin/in-°F	DIN 53752
Thermal Conductivity	0.390 W/m-K	2.71 BTU-in/hr-ft²-°F	DIN 52612
Maximum Service Temperature, Air	120 °C	248 °F
	160 °C	320 °F	short term
Deflection Temperature at 1.8 MPa (264 psi)	249 °C	480 °F
Vicat Softening Point	250 °C	482 °F	DIN ISO 306

Electrical Properties	Metric	English	Comments
Surface Resistance	10000 ohm	10000 ohm
Insulation Resistance	10000 ohm	10000 ohm

Processing Properties	Metric	English	Comments
Processing Temperature	290 °C	554 °F	mass temp
Nozzle Temperature	280 - 300 °C	536 - 572 °F
Zone 1	290 - 310 °C	554 - 590 °F
Zone 2	290 - 310 °C	554 - 590 °F
Zone 3	290 - 310 °C	554 - 590 °F
Mold Temperature	90.0 - 120 °C	194 - 248 °F
Drying Temperature	75.0 °C @Time 21600 - 57600 sec	167 °F @Time 6.00 - 16.0 hour	Dehumidifying dryer
	105 °C @Time 14400 - 21600 sec	221 °F @Time 4.00 - 6.00 hour	Vacuum Dryer

Descriptive Properties	Value	Comments
Color	natural color (black)