Lanxess Pocan® T 7391 POS151 900044 PBT + PET, 45% Glass Fiber
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET) |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® T 7391 POS151 900044 PBT + PET, 45% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT + PET, 45% glass fibers, injection molding, improved surface finish, increased temperature peak load UV stabilizedInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.69 g/cc | 1.69 g/cc | ISO 1183 |
| Bulk Density | 0.800 g/cc | 0.0289 lb/in³ | ISO 60 |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.30 % | 0.30 % | ISO 62 |
| Viscosity Test | 80 cm³/g | 80 cm³/g | Viscosity number; ISO 1628-5 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0020 cm/cm | 0.0020 in/in | 60x60x2; 270°C / MT 90°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0080 cm/cm | 0.0080 in/in | 60x60x2; 270°C / MT 90°C; 600 bar; ISO 294-4 | |
| Melt Flow | 30 g/10 min @Load 5.00 kg, Temperature 260 °C |
30 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133-1 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 250 MPa | 36300 psi | ISO 2039-1 |
| Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527-1, -2; 5 mm/min |
| Elongation at Break | 1.9 % | 1.9 % | ISO 527-1, -2; 5 mm/min |
| Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527-1, -2; 1 mm/min |
| Flexural Strength | 260 MPa @Strain 2.10 % |
37700 psi @Strain 2.10 % |
2 mm/min; ISO 178-A |
| Flexural Modulus | 15.5 GPa | 2250 ksi | 2 mm/min; ISO 178-A |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1U |
| 60.0 kJ/m² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U | |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| 6.50 J/cm² @Temperature -30.0 °C |
30.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA | |
| Tensile Creep Modulus, 1 hour | 16500 MPa | 2.39e+6 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 15000 MPa | 2.18e+6 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Thermal Conductivity | 0.270 W/m-K | 1.87 BTU-in/hr-ft²-°F | ISO 8302 |
| Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1, -3 |
| Maximum Service Temperature, Air | 150 °C | 302 °F | IEC 60216-1, Tensile impact strength, 20000 h |
| 155 °C | 311 °F | IEC 60216-1, Tensile strength, 20000 h | |
| 155 °C | 311 °F | IEC 60216-1, Electric strength, 20000 h | |
| 220 °C | 428 °F | Resistance to heat - ball pressure test; IEC 60695-10-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 150 °C | 302 °F | ISO 75-1, -2 |
| Vicat Softening Point | 210 °C @Load 5.10 kg |
410 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
||
| Oxygen Index | 21 % | 21 % | Method A; ISO 4589-2 |
| Glow Wire Test | 750 °C @Diameter 2.00 mm |
1380 °F @Diameter 0.0787 in |
GWFI; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 4.2 @Frequency 1.00e+6 Hz |
4.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.3 @Frequency 100 Hz |
4.3 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 28.0 kV/mm @Thickness 1.00 mm |
711 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.0020 @Frequency 100 Hz |
0.0020 @Frequency 100 Hz |
IEC 60250 |
| 0.014 @Frequency 1.00e+6 Hz |
0.014 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 250 V | 250 V | d.a.m.; Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| 270 °C | 518 °F | for test specimens; ISO 294 | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| 90.0 °C | 194 °F | for test specimens; ISO 294 | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 4 - 8 hour | 4 - 8 hour | |
| Moisture Content | 0.00 - 0.020 % | 0.00 - 0.020 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Electrolytic Corrosion | IEC 60426 | A 1 |
| Halving Interval (°C) | 10.2 | IEC 60216-1, Tensile strength |
| 10.2 | IEC 60216-1, Electric strength | |
| 13.5 | IEC 60216-1, Tensile impact strength | |
| ISO Shortname | ISO 7792-1-PBT+PET, GHLMR, 09-160, GF45 |
Users viewing this material also viewed the following:
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 20 PHR Carbon Black, N-990 (MT)
- KKPC Kumho KHS 68 High Styrene Resin Masterbatch (HSR)
- Lucite International Elvacite ® 3001 Acrylic Resin
- Unitika elitel UE3350 Polyester, Flake
- DuPont Vamac® GXF Sample Compound Vulcanizate Slab Cure (5 minutes at 190°C) Without Armeen® 18D
- TIMCAL TIMREX® PG10 Natural P/M Special-Graphite
- A. Schulman PP 3052X-01 Polypropylene Impact Resistant Copolymer
- Chengdu Polyster H4543B Thermoplastic Polyether-ester Elastomer (TPEE)
- Total Lacqtene® 1008 FE 30 LDPE blown film (discontinued **)
Copyright © lookpolymers.com All Rights Reserved