Lanxess Pocan® KU 2-7503/1 000000 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Extrusion Grade , Polybutylene Terephthalate (PBT), Flame Retardant , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® KU 2-7503/1 000000 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, non-reinforced, injection molding, extrusion, flame retardant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | Test Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0018 cm/cm | 0.0018 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0017 cm/cm | 0.0017 in/in | ISO 294-4, 2577 |
| Melt Flow | 19 g/10 min @Load 2.16 kg, Temperature 250 °C |
19 g/10 min @Load 4.76 lb, Temperature 482 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ISO 527-1/-2 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | ISO 527-1/-2 |
| Elongation at Break | 16 % | 16 % | ISO 527-1/-2 |
| Elongation at Yield | 7.0 % | 7.0 % | ISO 527-1/-2 |
| Tensile Modulus | 2.80 GPa | 406 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| >= 1.00 J/cm² @Temperature 23.0 °C |
>= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Tensile Creep Modulus, 1 hour | 2400 MPa | 348000 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 1400 MPa | 203000 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 48.0 °C | 118 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.4 @Frequency 100 Hz |
3.4 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0020 @Frequency 100 Hz |
0.0020 @Frequency 100 Hz |
IEC 60250 |
| 0.016 @Frequency 1.00e+6 Hz |
0.016 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Flame retarding agent | |
| Release agent | ||
| Features | Flame retardant | |
| Form | Pellets | |
| ISO Shortname | ISO 7792-1-PBT,GFHMR,11-030; ISO 1043-PBT FR(17) | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- SABIC PVC 67S Suspension Polyvinyl Chloride for Rigid Extruded Products
- Polymer Resources PC-FD2-[color]-1 Polycarbonate, FDA-compliant Feedstocks, Medium Flow with Mold Release, Gamma Resistant
- PolyOne Edgetek® 5209 Black 30 A 1 Acetal (POM) Copolymer
- Mid-Mountain Materials CERMEX® MT1000 Needled Fiberglass Mat
- Saint-Gobain Chemfab® 6 Primary PTFE-Coated Glass
- Chi Mei Kibiton® PB-575 SBC
- Denka LCS Z1070 Thermoplastic Elastomer, Extrusion grade (general)
- Chi Mei Kibiton® PB-5925 SBC
- BASF Ultramid® A3X2G5 25% Glass Filled PA66 (Dry)
- SMAC CABLE® 2525S-30-08 Damping Material
Copyright © lookpolymers.com All Rights Reserved