Solvay TECHNYL® A 208KBK-10N-L PA66, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 208KBK-10N-L PA66, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide 66, highly UV-resistance, toughness modified for injection molding.Available in: Asia PacificProduct Applications: TECHNYL A 208K BK 10N-L is used in all sectors of industry, offering on excellent UV resistance, toughness, well balanced mechanical property etc. This grade is used for cable-tie, fastener. This product is available in Black color.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Water Absorption | 1.2 % @Temperature 23.0 °C, Time 86400 sec |
1.2 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.019 cm/cm | 0.019 in/in | |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D786 |
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | ASTM D6368 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 118 MPa | 17100 psi | ASTM D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
| Izod Impact, Notched | 0.620 J/cm | 1.16 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 262 °C | 504 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 73.0 °C | 163 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C | 412 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.9 | 2.9 | IEC 60250 |
| Dissipation Factor | 0.030 | 0.030 | IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 265 - 285 °C | 509 - 545 °F | |
| Front Barrel Temperature | 275 - 295 °C | 527 - 563 °F | |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-290°C |
Users viewing this material also viewed the following:
- ExxonMobil Optema® TC-221 Ethylene Methyl Acrylate for Compounding (discontinued **)
- Chosun Refractories C18A Magnesia Carbon Brick for Converter
- ConocoPhillips Hydroclear® 22 Ultra-Clean Spindle Oil
- ConocoPhillips Hydroclear® 320 Circulating Oil
- DSM Arnite® AV2 372 PET-35% Glass Reinforced (European and Asian Grade)
- AIM 80In/Pb15/Ag5 Solder for Photonic Packaging
- Cheng Yu Plastic E2325 Flame Retardant PET, 25% Glass Fiber
- A. Schulman ComAlloy Hiloy® 415 Polyester - PBT, Glass Reinforced
- Arlon 47561R007 0.0075" (0.190 mm) Uncured Rubber
Copyright © lookpolymers.com All Rights Reserved