Supreme Petrochem SP 566 Flame Retardant Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Flame Retardant |
| Manufacturer | Supreme Petrochem LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Supreme Petrochem SP 566 Flame Retardant Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics Good flow and toughness Free of DBDPO, PBDE & TBBA, complies with ROHS directive of EU Available in any color Processing Extrusion MoldingApplications Large size T.V. Cabinets Electrical appliance parts, business machines Sheets for mass transit furnishing etc. Material Status: Commercial : ActiveAgency Ratings: UL 94 file E 185934Information provided by Supreme Petrochem LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Melt Flow | 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 27.5 MPa | 3990 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 40 % | 40 % | 50 mm/min; ASTM D638 |
| Flexural Strength | 34.3 MPa @Thickness 3.20 mm |
4970 psi @Thickness 0.126 in |
ASTM D790 |
| Flexural Modulus | 1.77 GPa @Thickness 3.20 mm |
256 ksi @Thickness 0.126 in |
ASTM D790 |
| Izod Impact, Notched | 1.00 J/cm @Thickness 3.20 mm |
1.87 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Vicat Softening Point | 97.0 °C | 207 °F | 1kg / 120°C; ASTM D1525 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Glow Wire Test | 850 °C | 1560 °F | IEC 695-2-1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 93 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 93 |
| Dielectric Constant | 2.6 @Frequency 1e+6 Hz |
2.6 @Frequency 1e+6 Hz |
IEC 250 |
| Dissipation Factor | 0.00040 @Frequency 1e+6 Hz |
0.00040 @Frequency 1e+6 Hz |
IEC 250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | <= 250 °C | <= 482 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Pre drying temp. |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH GF12030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- Nilit FRIANYL B63 KV20 Nylon 6 for injection molding, 20% glass ball reinforced
- PolyChem Alloy PolyFoam DCE5
- PolyMirae Moplen EP540T Injection Molding Grade Polypropylene
- Lehmann & Voss LUVOCOM® 1105-7740 PEEK, lubricant modified, heat stabilized
- Samsung Cheil Industries Starex® VE-1805 HIPS, Unreinforced FR
- China Tungsten Kmo47-B Molybdenum Concentrate
- ExxonMobil Santoprene® 123-50W175 Thermoplastic Elastomer
- Colorite Polymers 9511G-015 (Extrustion), 9512G-015 (Molding) Radiation Sterilizable Vinyl Compound
- ATI Allegheny Ludlum AL 400™ Nickel-Base Alloy, Hot Rolled Plate, UNS N04400
Copyright © lookpolymers.com All Rights Reserved