Lanxess Durethan® DP BKV 60 EF 000000 Nylon6, 60% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 60% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® DP BKV 60 EF 000000 Nylon6, 60% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, 60% glass fibers, injection molding, improved flowabilityInformation provided by LANXESS.
Physical Properties Metric English Comments
Linear Mold Shrinkage, Flow 0.00020 cm/cm
0.00020 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0020 cm/cm
0.0020 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.00060 cm/cm
0.00060 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0020 cm/cm
0.0020 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 158 MPa
22900 psi
cond.; ISO 527-1, -2; 5 mm/min
230 MPa
33400 psi
d.a.m.; ISO 527-1, -2; 5 mm/min
Elongation at Break 2.5 %
2.5 %
d.a.m.; ISO 527-1, -2; 5 mm/min
3.5 %
3.5 %
cond.; ISO 527-1, -2; 5 mm/min
Tensile Modulus 12.5 GPa
1810 ksi
cond.; ISO 527-1, -2; 1 mm/min
20.0 GPa
2900 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 390 MPa

@Strain 3.00 %
 56600 psi

@Strain 3.00 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Modulus 20.2 GPa
2930 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) 18.0 kJ/m²

@Temperature 23.0 °C
 8.57 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1A
18.0 kJ/m²

@Temperature -30.0 °C
 8.57 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 180-1A
Izod Impact, Unnotched (ISO) 90.0 kJ/m²

@Temperature 23.0 °C
 42.8 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1U
90.0 kJ/m²

@Temperature 23.0 °C
 42.8 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 180-1U
90.0 kJ/m²

@Temperature -30.0 °C
 42.8 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1U
90.0 kJ/m²

@Temperature -30.0 °C
 42.8 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 180-1U
Charpy Impact Unnotched 9.50 J/cm²

@Temperature 23.0 °C
 45.2 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eU
9.50 J/cm²

@Temperature -30.0 °C
 45.2 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eU
Charpy Impact, Notched 1.70 J/cm²

@Temperature 23.0 °C
 8.09 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eA
1.70 J/cm²

@Temperature -30.0 °C
 8.09 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eA
Puncture Energy 3.70 J

@Load <=133 kg,
Temperature -30.0 °C
 2.73 ft-lb

@Load <=292 lb,
Temperature -22.0 °F
 ISO 6603-2
4.30 J

@Load <=140 kg,
Temperature 23.0 °C
 3.17 ft-lb

@Load <=308 lb,
Temperature 73.4 °F
 ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 10.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 5.56 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 44.4 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Melting Point 221 °C
430 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 222 °C
432 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 213 °C
415 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
280 °C
536 °F
for test specimens; ISO 294
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 120 °C
176 - 248 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.060 - 0.20 %
0.060 - 0.20 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 1874-PA 6, GHR, 10-190, GF60