Lanxess Durethan® DP 2325 H3.0 DUS031 000000 Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP 2325 H3.0 DUS031 000000 Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, non-reinforced, injection molding, improved flowability, impact modified, heat-aging stabilizedInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.076 g/cc | 1.076 g/cc | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | d.a.m.; ISO 527-1, -2; 5 mm/min |
| Elongation at Break | 80 % | 80 % | d.a.m.; ISO 527-1, -2; 5 mm/min |
| Tensile Modulus | 2.00 GPa | 290 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min |
| Flexural Strength | 74.0 MPa @Strain 7.10 % |
10700 psi @Strain 7.10 % |
d.a.m., 2 mm/min; ISO 178-A |
| Flexural Yield Strength | 61.0 MPa @Strain 3.50 % |
8850 psi @Strain 3.50 % |
d.a.m., 2 mm/min; ISO 178-A |
| Flexural Modulus | 1.90 GPa | 276 ksi | d.a.m., 2 mm/min; ISO 178-A |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 180-1A |
| 80.0 kJ/m² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1A | |
| 90.0 kJ/m² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | d.a.m.; ISO 180-1U |
| NB | NB | cond.; ISO 180-1U | |
| Charpy Impact Unnotched | NB | NB | d.a.m.; ISO 179-1eU |
| NB | NB | cond.; ISO 179-1eU | |
| Charpy Impact, Notched | 2.20 J/cm² @Temperature -30.0 °C |
10.5 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eA |
| 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eA | |
| 11.0 J/cm² @Temperature 23.0 °C |
52.3 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | 10°C/min; ISO 11357-1, -3 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | admissible residence time at Tmax >= 10 min |
| 280 °C | 536 °F | for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 90.0 °C | 176 - 194 °F | ||
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 66-HI, GHR, 12-020 |
Users viewing this material also viewed the following:
- Network Polymers Softflex® 0250
- LyondellBasell Petrothene® PR92735 Linear Low Density Polyethylene
- Huntsman HY 5200 Aromatic Amine
- Techmer ES Plastiblend® PSU CR X
- SABIC Innovative Plastics LNP THERMOCOMP LF002 PEEK (Europe-Africa-Middle East)
- Süd-Chemie Nanofil® 15 Flame Retardant
- Hippe POM Copolymer
- 3M Cushion-Mount™ E1860H Plus Plate Mounting Tapes with Easy Mount Adhesive and High Plateside Adhesion
- 3M RJS-5 3/C Phase Rejacketing System
- Asahi Kasei Tenac® LA543 Homopolymer Acetal Resin
Copyright © lookpolymers.com All Rights Reserved