Lanxess Durethan® BM 40 X H2.0 DUS009 901510 Nylon 6, 40% Glass Fiber + Mineral
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BM 40 X H2.0 DUS009 901510 Nylon 6, 40% Glass Fiber + Mineral.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, injection molding grade, 40% glass fibers/mineral, good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Viscosity Test | 138 cm³/g | 138 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Linear Mold Shrinkage, Flow | 0.0051 cm/cm | 0.0051 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0067 cm/cm | 0.0067 in/in | ISO 294-4, 2577 |
| Melt Flow | 27 g/10 min @Load 5.00 kg, Temperature 260 °C |
27 g/10 min @Load 11.0 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | Conditioned; ISO 527-1/-2 |
| 120 MPa | 17400 psi | ISO 527-1/-2 | |
| Elongation at Break | 2.8 % | 2.8 % | ISO 527-1/-2 |
| Tensile Modulus | 4.00 GPa | 580 ksi | Conditioned; ISO 527-1/-2 |
| 8.00 GPa | 1160 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Impact | 568 | 568 | Puncture maximum force (N); ISO 6603-2 |
| 602 @Temperature -30.0 °C |
602 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 1.40 J | 1.03 ft-lb | ISO 6603-2 |
| 1.50 J @Temperature -30.0 °C |
1.11 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 1.50 J @Temperature -30.0 °C |
1.11 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 221 °C | 430 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 80.0 °C | 176 °F | ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 425 V | 425 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6,MHR,14-080,(GF+MD)40 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 4008 T Polypropylene
- Polymax® Maxelast® P3880 TPE, PP Overmold or Standalone use
- SABIC Innovative Plastics GELOY XP4034 ASA+PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics ULTEM 2100R PEI (Asia Pacific)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with DOP Plasticizer
- Polyplastics Duranex® 6300B Polybutylene Terephthalate (PBT), Anisotropy improvement, 30% GB filled
- Dow Buna® SB 1502 Cold polymerized Emulsion Styrene Butadiene Rubber (E-SBR)
- CLAL-MSX ARCAP Anticorrosion AP4 H15 Spring, Drawn Copper Alloy
- Clariant PA123G30 Nylon 66, 30% Glass Fiber, Impact Modified, Heat Stabilized
- Bhansali Engineering Santron IMS1000 SAN Resin
Copyright © lookpolymers.com All Rights Reserved