Arkema Group Orgalloy® LT 4060IH Flexible Nylon Alloy (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon, Flexible Alloy
Manufacturer	Arkema
Trade Name	Orgalloy®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Orgalloy® LT 4060IH Flexible Nylon Alloy (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Very flexible polyamide alloy: easy to process, low moisture absorption, good mechanical properties at low temperature. Demonstrate a good balance of properties eg, high flexibility (200 MPa), good thermal performance and ductility at low temperatures. Fame retardant with halogen (cable covering).ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Water Absorption	4.2 %	4.2 %
Moisture Absorption at Equilibrium	1.1 %	1.1 %	Humidity Absorption
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 235 °C	7.0 g/10 min @Load 4.76 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	21.0 MPa	3050 psi	50 mm/min
Elongation at Break	>= 50 %	>= 50 %	Nominal Strain; 50 mm/min
Tensile Modulus	0.300 GPa	43.5 ksi	1 mm/min
Charpy Impact, Notched	8.20 J/cm²	39.0 ft-lb/in²
	0.900 J/cm² @Temperature -30.0 °C	4.28 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10°C/min
Flammability, UL94	V-2 @Thickness 1.60 mm	V-2 @Thickness 0.0630 in
	V-0 @Thickness 3.20 mm	V-0 @Thickness 0.126 in

Electrical Properties	Metric	English
Electrical Resistivity	2.00e+14 ohm-cm	2.00e+14 ohm-cm
Surface Resistance	1.30e+13 ohm	1.30e+13 ohm
Dielectric Constant	3.1 @Frequency 1e+6 Hz	3.1 @Frequency 1e+6 Hz
	4.8 @Frequency 100 Hz	4.8 @Frequency 100 Hz
Dielectric Strength	39.0 kV/mm	991 kV/in
Dissipation Factor	0.0060 @Frequency 1e+6 Hz	0.0060 @Frequency 1e+6 Hz
	0.123 @Frequency 100 Hz	0.123 @Frequency 100 Hz
Comparative Tracking Index	600 V	600 V