Lucky EH-910 Acrylic, Extrusion Grade

Category	Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Heat Resistant, Molded
Manufacturer	Lucky
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lucky EH-910 Acrylic, Extrusion Grade.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Highest heat and stress cracking resistance of Lucky PMMA grades. Recommended for extrusion of sheets, pipes, and profiles. Can also be used for injection molding of small parts. May be UV stabilized. General Lucky PMMA qualities: Transparent/elegant appearance, high heat and weather resistance, excellent chemical resistance and coloring capability.

Physical Properties	Metric	English	Comments
Density	1.18 g/cc	0.0426 lb/in³	ASTM D792
Linear Mold Shrinkage	0.0020 - 0.0060 cm/cm	0.0020 - 0.0060 in/in	ASTM D955-51
Melt Flow	1.0 g/10 min	1.0 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	97	97	ASTM D785
Tensile Strength, Ultimate	74.0 MPa	10700 psi	ASTM D638
Elongation at Break	3.5 %	3.5 %	ASTM D638
Flexural Yield Strength	133 MPa	19300 psi	ASTM D790
Flexural Modulus	3.30 GPa	479 ksi	ASTM D790

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	98.0 °C	208 °F	Heat Distortion Temp
	98.0 °C	208 °F	Deflection Temp; Load not reported; ASTM D648
Vicat Softening Point	105 °C	221 °F	ASTM D1525
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.17 mm	HB @Thickness 0.125 in

Optical Properties	Metric	English	Comments
Refractive Index	1.49	1.49	ASTM D542
Transmission, Visible	92 %	92 %	ASTM D1003

Electrical Properties	Metric	English	Comments
Dielectric Strength	20.0 kV/mm	508 kV/in	ASTM D149