- Lanxess Durethan® BKV 15 000000 Copolyamide, 15% Glass Fiber
Lanxess Durethan® BKV 15 000000 Copolyamide, 15% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 15 000000 Copolyamide, 15% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CoPA, injection molding grade, 15% glass fibers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Water Absorption | 8.5 % | 8.5 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 2.6 % | 2.6 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Viscosity Test | 138 cm³/g | 138 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Conditioned; ISO 527-1/-2 |
| 125 MPa | 18100 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| 12 % | 12 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 3.60 GPa | 522 ksi | Conditioned; ISO 527-1/-2 |
| 6.30 GPa | 914 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 3.50 J/cm² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Impact | 6444 | 6444 | Puncture maximum force (N); ISO 6603-2 |
| 585 @Temperature -30.0 °C |
585 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 4.00 J | 2.95 ft-lb | ISO 6603-2 |
| 3.00 J @Temperature -30.0 °C |
2.21 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 3.00 J @Temperature -30.0 °C |
2.21 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 213 °C | 415 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 60.0 °C | 140 °F | ISO 75-1/-2 |
| Vicat Softening Point | 200 °C | 392 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
IEC 60695-11-10 | |
| Oxygen Index | 22 % | 22 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
IEC 60250 | |
| 5.0 @Frequency 1.00e+6 Hz |
5.0 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 10 @Frequency 100 Hz |
10 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | Conditioned; IEC 60243-1 |
| 40.0 kV/mm | 1020 kV/in | IEC 60243-1 | |
| Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.12 @Frequency 1.00e+6 Hz |
0.12 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.20 @Frequency 100 Hz |
0.20 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6/66, MR, 14-060, GF15 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8610 (496) (UF) Synthetic Oil
- Polimeri Europa Europrene® SOL T 172 Styrene - Butadiene Block Copolymer
- DuPont Performance Polymers Zytel® 70G30L NC010 Nylon 66 (Unverified Data**)
- Kinlead PG14 Bag Grade BOPP Plain Film (thickness: 40 µm)
- Shin-Etsu Silicones LIMSâ„¢ KE1950-30A/B Elastomer
- A. Schulman POLYBATCH™ Yellow 2200 Concentrate Based In Polyethylene
- Eifeler Coatings Technology TiC/TiN CVD Coating
- Braskem TS9022 Blown Film Extrusion Low Density Polyethylene
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 330ºF Cure Temperature
- Silberline Sparkle Silvet® 764-30-E1
Copyright © lookpolymers.com All Rights Reserved