Lanxess Durethan® BKV 140 DUS008 000000 Nylon 6, 40% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled , Nylon 6, Glass Filled, Impact Grade
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 140 DUS008 000000 Nylon 6, 40% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, 40% glass fibers, injection molding, impact modifiedInformation provided by LANXESS.
Physical Properties Metric English Comments
Linear Mold Shrinkage, Flow 0.0021 cm/cm
0.0021 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0075 cm/cm
0.0075 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 185 MPa
26800 psi
5 mm/min; ISO 527-1,-2
Elongation at Break 3.4 %
3.4 %
5 mm/min; ISO 527-1,-2
Tensile Modulus 12.0 GPa
1740 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 290 MPa
42100 psi
2 mm/min; ISO 178-A
Flexural Modulus 11.0 GPa
1600 ksi
2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) 11.0 kJ/m²

@Temperature 23.0 °C
 5.23 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
Izod Impact, Unnotched (ISO) 90.0 kJ/m²

@Temperature 23.0 °C
 42.8 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1U
90.0 kJ/m²

@Temperature -30.0 °C
 42.8 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1U
Charpy Impact Unnotched 10.0 J/cm²

@Temperature -30.0 °C
 47.6 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eU
10.5 J/cm²

@Temperature 23.0 °C
 50.0 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eU
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eA
1.50 J/cm²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eA
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 °C/min; ISO 11357-1,-3
Deflection Temperature at 0.46 MPa (66 psi) 217 °C
423 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 201 °C
394 °F
ISO 75-1,-2
Shrinkage 0.0700 %

@Temperature 120 °C,
Time 14400 sec
 0.0700 %

@Temperature 248 °F,
Time 4.00 hour
 post-shrinkage, transverse, 60x60x2; ISO 294-4
0.0900 %

@Temperature 120 °C,
Time 14400 sec
 0.0900 %

@Temperature 248 °F,
Time 4.00 hour
 post-shrinkage, 60x60x2; ISO 294-4
Processing Properties Metric English Comments
Melt Temperature 290 °C
554 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Dry Time 2.00 - 6.00 hour

@Temperature 80.0 °C
 2.00 - 6.00 hour

@Temperature 176 °F
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
Karl Fischer test