Gouda Vuurvast VIBRON 150 G RAPID Dense Vibrating Refractory Castable

Category Ceramic , Oxide , Aluminum Oxide
Manufacturer Gouda Vuurvast
Trade Name VIBRON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Gouda Vuurvast VIBRON 150 G RAPID Dense Vibrating Refractory Castable.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Vibron 150 G Rapid is a low cement castable based on sintered South-American bauxite. Because of special additives this material is suited for direct contact with liquid aluminum and allows a shorter heating schedule. Applied for aluminum furnaces, launders and ladles.Remarks: Indicated values apply to vibrated products.Information provided by Gouda Vuurvast.
Physical Properties Metric English Comments
Bulk Density 2.85 - 2.95 g/cc
0.103 - 0.107 lb/in³
After drying at 110°C
Particle Size <= 4000 µm
<= 4000 µm
Grain Size
Mechanical Properties Metric English Comments
Compressive Strength 80.0 - 90.0 MPa

@Temperature 100 °C
11600 - 13100 psi

@Temperature 212 °F
Cold Crushing Strength
105 - 115 MPa

@Temperature 1300 °C
15200 - 16700 psi

@Temperature 2370 °F
Cold Crushing Strength
Thermal Properties Metric English Comments
Thermal Conductivity 1.82 - 1.92 W/m-K

@Temperature 100 °C
12.6 - 13.3 BTU-in/hr-ft²-°F

@Temperature 212 °F
1.82 - 1.92 W/m-K

@Temperature 600 °C
12.6 - 13.3 BTU-in/hr-ft²-°F

@Temperature 1110 °F
1.89 - 1.99 W/m-K

@Temperature 1300 °C
13.1 - 13.8 BTU-in/hr-ft²-°F

@Temperature 2370 °F
Maximum Service Temperature, Air 1350 °C
2460 °F
Shrinkage -0.300 - 0.300 %

@Temperature 1300 °C
-0.300 - 0.300 %

@Temperature 2370 °F
Permanent Linear Change
Component Elements Properties Metric English Comments
Al2O3 76 %
76 %
Fe2O3 1.2 %
1.2 %
SiO2 12 %
12 %
Descriptive Properties Value Comments
Material Consumption per 1 m3 2850 kg
Mixing Water 5-6 liters
per 100 kgs dry material