Lanxess Durethan® BG 30 X H2.0 901510 Nylon 6, 30% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BG 30 X H2.0 901510 Nylon 6, 30% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, injection molding grade, 30% glass fibers/glass spheres, good surface, good heat-ageing resistance
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
Water Absorption 7.0 %
7.0 %
Test Sim. to ISO 62
Moisture Absorption at Equilibrium 2.2 %
2.2 %
23°C/50% R.H.; Test Sim. to ISO 62
Viscosity Test 140 cm³/g
140 cm³/g
Viscosity number; ISO 307, 1157, 1628
Melt Flow 35 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 35 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 Calculated from MVR using melt density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
Conditioned; ISO 527-1/-2
120 MPa
17400 psi
ISO 527-1/-2
Elongation at Break 3.5 %
3.5 %
ISO 527-1/-2
10 %
10 %
Conditioned; ISO 527-1/-2
Tensile Modulus 3.10 GPa
450 ksi
Conditioned; ISO 527-1/-2
6.30 GPa
914 ksi
ISO 527-1/-2
Charpy Impact Unnotched 3.50 J/cm²

@Temperature -30.0 °C
 16.7 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
3.50 J/cm²

@Temperature -30.0 °C
 16.7 ft-lb/in²

@Temperature -22.0 °F
 Conditioned; ISO 179/1eU
3.50 J/cm²

@Temperature 23.0 °C
 16.7 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
7.00 J/cm²

@Temperature 23.0 °C
 33.3 ft-lb/in²

@Temperature 73.4 °F
 Conditioned; ISO 179/1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 Conditioned; ISO 179/1eA
<= 1.00 J/cm²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
<= 1.00 J/cm²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 Conditioned; ISO 179/1eA
Impact 680
680
Puncture maximum force (N); ISO 6603-2
650

@Temperature -30.0 °C
 650

@Temperature -22.0 °F
 Puncture maximum force (N); ISO 6603-2
Puncture Energy 2.30 J
1.70 ft-lb
ISO 6603-2
2.00 J

@Temperature -30.0 °C
 1.48 ft-lb

@Temperature -22.0 °F
 ISO 6603-2
2.00 J

@Temperature -30.0 °C
 1.48 ft-lb

@Temperature -22.0 °F
 Conditioned; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C
16.7 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C
50.0 µin/in-°F
ISO 11359-1/-2
Melting Point 222 °C
432 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 60.0 °C
140 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 IEC 60695-11-10
HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
 IEC 60695-11-10
Oxygen Index 23 %
23 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Dielectric Constant 4.0

@Frequency 1.00e+6 Hz
 4.0

@Frequency 1.00e+6 Hz
 IEC 60250
4.5

@Frequency 100 Hz
 4.5

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 33.0 kV/mm
838 kV/in
IEC 60243-1
Dissipation Factor 0.0189

@Frequency 1.00e+6 Hz
 0.0189

@Frequency 1.00e+6 Hz
 IEC 60250
0.0223

@Frequency 100 Hz
 0.0223

@Frequency 100 Hz
 IEC 60250
Comparative Tracking Index 325 V
325 V
IEC 60112
Descriptive Properties Value Comments
Additives Release agent
Features Heat stabilized or stable to heat
Form Pellets
ISO Shortname ISO 1874-PA 6, MHR,14-060, (GB+GF)30
Processing Injection molding
Region Asia Pacific
Europe
Near East/Africa
North America
South and Central America