NOVA Chemicals Novapol® TR-0535-UIG Hexene MDPE Rotational Molding Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , MDPE , Medium Density Polyethylene (MDPE), Rotational Molded
Manufacturer NOVA Chemicals
Trade Name Novapol®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Novapol® TR-0535-UIG Hexene MDPE Rotational Molding Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TR-0530-UIG complies with the U.S. FDA specifications for olefin polymers and may be used in the U.S. as an article or component of an article intended for use in contact with food. TR-0530-UIG is subject to the specific limitations that it may contain food only in articles having a volume of at least 18.9 L (5 gal. U.S.), only at temperatures of 150°F and below, and may not be used to hold ready-prepared foods intended to be reheated in the container at time of use. It is biologically and chemically inert.Features: Excellent low temperature impact properties, Excellent ESCR, Wide process window, Retention of impact @ long cook times, NSF listed for Stds. 24 & 61, UL 94 HB Additives: Processing antioxidants, UV stabilizersApplications: IBCs, Toys, General Purpose custom molding, Agricultural storage tanks, Marine parts
Physical Properties Metric English Comments
Density 0.935 g/cc
0.0338 lb/in³
ASTM D 792
ESCR 100% Igepal® >= 1000 hour

@Temperature 50.0 °C
>= 1000 hour

@Temperature 122 °F
Bent Strip, Condition A & B, F50 values, From compression molded samples; ASTM D 1693
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 17.5 MPa

@Thickness 1.91 mm
2540 psi

@Thickness 0.0750 in
Type IV specimen, 2" per minute test speed, compression molded sample; ASTM D 638
Elongation at Yield 12 %

@Thickness 1.91 mm
12 %

@Thickness 0.0750 in
Type IV specimen, 2" per minute test speed, compression molded sample; ASTM D 648
Flexural Modulus 0.680 GPa
98.6 ksi
1% Strain Value, From compression molded samples; ASTM D 790
Impact Test 67.8 J

@Thickness 3.17 mm,
Temperature -40.0 °C
50.0 ft-lb

@Thickness 0.125 in,
Temperature -40.0 °F
Rotomolded samples; ARM Method
217 J

@Thickness 0.250 mm,
Temperature -40.0 °C
160 ft-lb

@Thickness 0.00984 in,
Temperature -40.0 °F
Rotomolded samples; ARM Method
Thermal Properties Metric English Comments
Melting Point 125 °C
257 °F
ASTM E 794
Deflection Temperature at 0.46 MPa (66 psi) 58.0 °C
136 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 42.0 °C
108 °F
ASTM D 648
Processing Properties Metric English Comments
Melt Temperature 204 - 315 °C
399 - 599 °F
Recommended oven temperature