Lanxess Durethan® B 30 S FN40 000000 Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® B 30 S FN40 000000 Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, injection molding grade, non- reinforced, good flowability, easy-release, fast cycling, UL 94V-2 off 0,75 mm, GWIT 775°C bei 0,75/1,5mm
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Water Absorption | 10 % | 10 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 3.0 % | 3.0 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Viscosity Test | 138 cm³/g | 138 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4, 2577 |
| Melt Flow | 32 g/10 min @Load 5.00 kg, Temperature 260 °C |
32 g/10 min @Load 11.0 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527-1/-2 |
| 65.0 MPa | 9430 psi | Conditioned; ISO 527-1/-2 | |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | Conditioned; ISO 527-1/-2 |
| 90.0 MPa | 13100 psi | ISO 527-1/-2 | |
| Elongation at Break | 9.6 % | 9.6 % | Nominal; ISO 527-1/-2 |
| 15.5 % | 15.5 % | ISO 527-1/-2 | |
| 265 % | 265 % | Nominal, Conditioned; ISO 527-1/-2 | |
| 293 % | 293 % | Conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-1/-2 |
| 22.5 % | 22.5 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 1.10 GPa | 160 ksi | Conditioned; ISO 527-1/-2 |
| 3.40 GPa | 493 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 331 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
IEC 60695-11-10 |
| Oxygen Index | 28 % | 28 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Flame retarding agent | |
| Features | Flame retardant | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6,MFR,14-030N; ISO 1043-PA FR(30) | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP THERMOCOMP RF006S PA6.6 (Europe-Africa-Middle East)
- Solvay SOPROPHOR® CY/8 Surfactant
- A. Schulman POLYBATCH™ Dark Blue Oil LL40350/4 Concentrate Based In LLDPE
- EMS-Grivory Grivory® HT2V-3H LF PA*-GF30
- ExxonMobil Metallyte™ 18MM483 OPP Film
- Covestro Makroblend® DP 2-7655 Polycarbonate + PET, Mineral Filled Impact Grade
- China Tungsten ZK10 Tungsten Carbide
- Aquabond Technologies Aquabond™ ABS-65 Water Soluble Adhesive and Bonding Thermoplastic
- 3M Scotch-Weld™ 3750 Tan Hot Melt Adhesive
Copyright © lookpolymers.com All Rights Reserved