Covestro Bayblend® FR 3006 Polycarbonate + ABS, Flame Retardant Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Covestro |
| Trade Name | Bayblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Covestro Bayblend® FR 3006 Polycarbonate + ABS, Flame Retardant Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection molding gradehigh heat resistanceVicat/B 120 = 110 °Ceasy flowUL-listing 94 V-1 at 1.5 mm and V-0 at 2.0 mmPreprocessingMax. Water content
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Water Absorption | 0.50 % | 0.50 % | Similar to ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | Similar to ISO 62 |
| Melt Flow | 38 g/10 min @Load 5.00 kg, Temperature 240 °C |
38 g/10 min @Load 11.0 lb, Temperature 464 °F |
estimated from MVR using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-1/-2 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-1/-2 |
| Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527-1/-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.0 µm/m-°C | 37.8 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 68.0 µm/m-°C | 37.8 µin/in-°F | ISO 11359-1/-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | ISO 75-1/-2 |
| Vicat Softening Point | 108 °C | 226 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
IEC 60695-11-10 |
| V-0 @Thickness 2.00 mm |
V-0 @Thickness 0.0787 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz |
3.1 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.2 @Frequency 100 Hz |
3.2 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
IEC 60250 |
| 0.0070 @Frequency 1.00e+6 Hz |
0.0070 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 350 V | 350 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 °C | 464 °F | Injection Molding; ISO 294 |
| 240 - 270 °C | 464 - 518 °F | ||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| 80.0 °C | 176 °F | Injection Molding; ISO 10724 | |
| Injection Velocity | 240 mm/sec | 9.45 in/sec | ISO 294 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Asia Pacific | |
| Europe | ||
| India | ||
| Near East/Africa | ||
| South and Central America | ||
| Feature | Release agent | |
| Form | Pellets | |
| Process | Injection Molding |
Users viewing this material also viewed the following:
- PSM Industries Pacific Sintered Metals Bronze BT-126 Powdered Metal
- Ineos Nova Zylar® 221 Clear Impact Modified Acrylic Copolymer (discontinued **)
- Kinlead PT11 Adhesive Tape Grade BOPP Plain Film (thickness: 28 µm)
- LG Chemical Lupox® GP2300R PBT+GF30%
- A. Schulman LP552-01 Injection Molding, Extrusion Grade Compound
- Dow Corning SYL-OFF® 7048 CROSSLINKER
- Eifeler Coatings Technology EXXTRAL® blue PVD Coating
- Fainplast Compounds PMS 60 Flexible PVC, Lead Free
- Axiall 19732 Wire & Cable Flexible PVC
- ACC ReactAmine® EP 350 EPI Engineered Polymers Polyurea
Copyright © lookpolymers.com All Rights Reserved