Clariant Renol TPU1088A Polyurethane Elastomer, Aromatic Polyester

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade
Manufacturer Clariant
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Clariant Renol TPU1088A Polyurethane Elastomer, Aromatic Polyester.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by Clariant Masterbatches
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0090 cm/cm
0.0090 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Shore A 88
88
ASTM D2240
Tensile Strength, Yield 42.1 MPa
6100 psi
ASTM D638
7.067 MPa

@Strain 100 %
 1025 psi

@Strain 100 %
 ASTM D412
Elongation at Break 375 %
375 %
ASTM D638
Flexural Modulus 0.0462 GPa
6.70 ksi
ASTM D790
Compression Set 14 %

@Temperature 23.0 °C,
Time 79200 sec
 14 %

@Temperature 73.4 °F,
Time 22.0 hour
 ASTM D648
49 %

@Temperature 70.0 °C,
Time 79200 sec
 49 %

@Temperature 158 °F,
Time 22.0 hour
 ASTM D648
Thermal Properties Metric English Comments
Vicat Softening Point 134 °C
274 °F
Rate A; ASTM D1526
Processing Properties Metric English Comments
Melt Temperature 193 - 210 °C
380 - 410 °F
Mold Temperature 37.8 - 65.6 °C
100 - 150 °F
Dry Time 2 - 4 hour

@Temperature 104 °C
 2 - 4 hour

@Temperature 220 °F
 to ensure moisture level is less than 0.02%
Injection Pressure 4.96 - 8.27 MPa
720 - 1200 psi
Secondary
8.27 - 13.8 MPa
1200 - 2000 psi
Initial
Back Pressure 0.000 - 0.345 MPa
0.000 - 50.0 psi
Shot Size 30 - 80 %
30 - 80 %
Screw Speed 20 - 100 rpm
20 - 100 rpm