Lanxess Durethan® AKV 15 000000 Nylon 66, 15% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® AKV 15 000000 Nylon 66, 15% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 66, injection molding grade, 15% glass fibers
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
ISO 1183
Water Absorption 7.0 %
7.0 %
Test Sim. to ISO 62
Moisture Absorption at Equilibrium 2.4 %
2.4 %
23°C/50% R.H.; Test Sim. to ISO 62
Viscosity Test 146 cm³/g
146 cm³/g
Viscosity number; ISO 307, 1157, 1628
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
Conditioned; ISO 527-1/-2
125 MPa
18100 psi
ISO 527-1/-2
Elongation at Break 3.0 %
3.0 %
ISO 527-1/-2
8.0 %
8.0 %
Conditioned; ISO 527-1/-2
Tensile Modulus 4.10 GPa
595 ksi
Conditioned; ISO 527-1/-2
6.70 GPa
972 ksi
ISO 527-1/-2
Charpy Impact Unnotched 4.00 J/cm²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
4.00 J/cm²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 Conditioned; ISO 179/1eU
4.00 J/cm²

@Temperature 23.0 °C
 19.0 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
5.00 J/cm²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
 Conditioned; ISO 179/1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 Conditioned; ISO 179/1eA
<= 1.00 J/cm²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
<= 1.00 J/cm²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 Conditioned; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C
22.2 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C
50.0 µin/in-°F
ISO 11359-1/-2
Melting Point 263 °C
505 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 70.0 °C
158 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 IEC 60695-11-10
HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
 IEC 60695-11-10
Oxygen Index 22 %
22 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
Conditioned; IEC 60093
1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
IEC 60093
Dielectric Constant 4.0

@Frequency 1.00e+6 Hz
 4.0

@Frequency 1.00e+6 Hz
 Conditioned; IEC 60250
4.0

@Frequency 1.00e+6 Hz
 4.0

@Frequency 1.00e+6 Hz
 IEC 60250
4.0

@Frequency 100 Hz
 4.0

@Frequency 100 Hz
 IEC 60250
9.0

@Frequency 100 Hz
 9.0

@Frequency 100 Hz
 Conditioned; IEC 60250
Dielectric Strength 30.0 kV/mm
762 kV/in
Conditioned; IEC 60243-1
35.0 kV/mm
889 kV/in
IEC 60243-1
Dissipation Factor 0.0080

@Frequency 100 Hz
 0.0080

@Frequency 100 Hz
 IEC 60250
0.015

@Frequency 1.00e+6 Hz
 0.015

@Frequency 1.00e+6 Hz
 IEC 60250
0.070

@Frequency 1.00e+6 Hz
 0.070

@Frequency 1.00e+6 Hz
 Conditioned; IEC 60250
0.13

@Frequency 100 Hz
 0.13

@Frequency 100 Hz
 Conditioned; IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Additives Release agent
Form Pellets
ISO Shortname ISO 1874-PA66, MR, 14-070, GF15
Processing Injection molding
Region Asia Pacific
Europe
Near East/Africa
North America
South and Central America