SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* LUBRICOMP* KP002 is a compound based on Acetal Copolymer resin containing 10% PTFE/Silicone. Added feature of this material is: Wear Resistant.

Physical Properties	Metric	English	Comments
Density	1.43 g/cc	0.0517 lb/inÂ³	ASTM D792
	1.43 g/cc	0.0517 lb/inÂ³	ISO 1183
Moisture Absorption	0.200 %	0.200 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.022 cm/cm @Time 86400 sec	0.022 in/in @Time 24.0 hour	ASTM D955
	0.022 cm/cm @Time 86400 sec	0.022 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.022 cm/cm @Time 86400 sec	0.022 in/in @Time 24.0 hour	ASTM D955
	0.022 cm/cm @Time 86400 sec	0.022 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	46.0 MPa	6670 psi	ASTM D638
Tensile Strength, Yield	46.0 MPa	6670 psi	ASTM D638
	46.0 MPa	6670 psi	ISO 527
Elongation at Break	40.9 %	40.9 %	ASTM D638
Elongation at Yield	26.3 %	26.3 %	ASTM D638
	29 %	29 %	ISO 527
Tensile Modulus	2.33 GPa	338 ksi	1 mm/min; ISO 527
	2.75 GPa	399 ksi	50 mm/min; ASTM D638
Flexural Strength	61.0 MPa	8850 psi	ISO 178
Flexural Modulus	2.00 GPa	290 ksi	ISO 178
	2.06 GPa	299 ksi	ASTM D790
Izod Impact, Notched	0.530 J/cm	0.993 ft-lb/in	ASTM D256
Izod Impact, Unnotched	10.68 J/cm	20.01 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	5.00 kJ/mÂ²	2.38 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	74.0 kJ/mÂ²	35.2 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	5.00 J	3.69 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	1.00 J	0.738 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.31	0.31	ASTM D3702 Modified
Coefficient of Friction, Static	0.18	0.18	ASTM D3702 Modified
K (wear) Factor	16.1 x 10^-8 mmÂ³/N-M	8.00 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	106 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	58.9 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	106 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	58.9 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	103 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	57.2 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	103 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	57.2 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	146 Â°C	295 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	156 Â°C @Thickness 3.20 mm	313 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	87.0 Â°C	189 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	92.0 Â°C @Thickness 3.20 mm	198 Â°F @Thickness 0.126 in	unannealed; ASTM D648