- Unitika TERRAMAC TE-8300 Polylactic Acid (PLA)
Unitika TERRAMAC TE-8300 Polylactic Acid (PLA)
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer |
| Manufacturer | Unitika |
| Trade Name | TERRAMAC |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika TERRAMAC TE-8300 Polylactic Acid (PLA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High-durability, Injection grade. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.0 MPa | 8120 psi | ISO 527 |
| Elongation at Break | 1.0 % | 1.0 % | ISO 527 |
| Flexural Strength | 104 MPa | 15100 psi | ISO 178 |
| Flexural Modulus | 9.30 GPa | 1350 ksi | ISO 178 |
| Charpy Impact, Notched | 0.280 J/cm² | 1.33 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 170 °C | 338 °F | |
| Maximum Service Temperature, Air | 240 °C | 464 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ISO 75 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 150 - 170 °C | 302 - 338 °F | |
| Middle Barrel Temperature | 180 - 200 °C | 356 - 392 °F | |
| Front Barrel Temperature | 190 - 210 °C | 374 - 410 °F | |
| Nozzle Temperature | 190 - 210 °C | 374 - 410 °F | |
| Mold Temperature | 100 - 110 °C | 212 - 230 °F | actual surface temp |
| Back Pressure | 0.490 - 1.47 MPa | 71.1 - 213 psi | gage pressure |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Opaque white |
Users viewing this material also viewed the following:
- Polymer Resources PC-HM-FR1-[color]-1 Polycarbonate, 10% Glass Reinforced, Flame Retardant with Mold Release
- ExxonMobil Escorene® LD-421 LDPE Power Cable Insulation (discontinued **)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N339 Filler
- LyondellBasell Petrothene® NA960070 Low Density Polyethylene
- Loxim 800 00 HB Polypropylene Compound, Flame Retardant
- Teknor Apex MONPRENE® MP 2860E Thermoplastic Elastomer
- Teknor Apex TEKRON® 4300-D88F Thermoplastic Elastomer
- DSM Akulon® K225-KS Nylon 6 (European and Asian Grade) (Cond)
- Ensinger Tecatron® XP-61 Compression Molded PPS Compound, 25% Fiberglass and Mineral Filled
- Permabond A126 Anaerobic Retainer
Copyright © lookpolymers.com All Rights Reserved