LG Chemical XR407D ABS

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer LG Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical XR407D ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Electric & Electronic HousingApplication: Electric & Electronic HousingCAS No. 25120-20-1, 9003-56-9, 25747-74-7, and 31621-07-5Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.07 g/cc
1.07 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 6.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 6.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 111
111
ASTM D785
Tensile Strength, Yield 47.1 MPa

@Thickness 3.20 mm
 6830 psi

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Break 20 %

@Thickness 3.20 mm
 20 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Flexural Yield Strength 77.5 MPa

@Thickness 3.20 mm
 11200 psi

@Thickness 0.126 in
 15 mm/min; ASTM D790
Flexural Modulus 2.45 GPa

@Thickness 3.20 mm
 356 ksi

@Thickness 0.126 in
 15 mm/min; ASTM D790
Izod Impact, Notched 1.57 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 2.94 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
1.67 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 3.12 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Izod Impact, Unnotched 0.785 J/cm

@Thickness 6.40 mm,
Temperature -30.0 °C
 1.47 ft-lb/in

@Thickness 0.252 in,
Temperature -22.0 °F
 ASTM D256
0.785 J/cm

@Thickness 3.20 mm,
Temperature -30.0 °C
 1.47 ft-lb/in

@Thickness 0.126 in,
Temperature -22.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 113 °C

@Thickness 6.40 mm
 235 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 104 °C

@Thickness 6.40 mm
 219 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Vicat Softening Point 111 °C

@Load 5.00 kg
 232 °F

@Load 11.0 lb
 50°C/h; ASTM D1525
UL RTI, Electrical 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
 UL 746B
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
 UL 746B
UL RTI, Mechanical with Impact 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
 UL 746B
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
 UL 746B
UL RTI, Mechanical without Impact 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
 UL 746B
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
 UL 746B
Flammability, UL94 HB

@Thickness >=1.50 mm
 HB

@Thickness >=0.0591 in
HB

@Thickness >=3.00 mm
 HB

@Thickness >=0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 180 - 220 °C
356 - 428 °F
Injection Molding
Middle Barrel Temperature 220 - 240 °C
428 - 464 °F
Injection Molding
Front Barrel Temperature 230 - 250 °C
446 - 482 °F
Injection Molding
Nozzle Temperature 240 - 250 °C
464 - 482 °F
Injection Molding
Melt Temperature 230 - 250 °C
446 - 482 °F
Injection Molding
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Injection Molding
Drying Temperature 80.0 - 90.0 °C
176 - 194 °F
Injection Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Molding
Back Pressure 1.96 - 3.92 MPa
284 - 569 psi
Injection Molding
Screw Speed 50 - 100 rpm
50 - 100 rpm
Injection Molding